Characterization of B4C-SiC ceramic composites prepared by ultra-high pressure sintering

Abstract

Additive-free boron carbide (B4C) – silicon carbide (SiC) ceramic composites with different B4C and β-SiC powders ratio were densified using the high-pressure “anvil-type with hollows” apparatus at 1500 °C under a pressure of 4 GPa for 60 s in air. The effect of starting powders ratio on the composites sintering behavior, relative density, microstructural development, and thermomechanical properties was studied. The sintered samples hardness was found to be in the range from 24 to 31 GPa. The thermal conductivity measurements, conducted in the temperature range from room temperature to 1000 °C, showed that the thermal diffusivity of sintered samples was between 6 and 9.5 mm2/s whereas the thermal conductivity was in the range from 16 to 28 W/(m K). The results of this study show that the high-pressure sintering can be a very effective low-temperature densification method for the obtainment of additive-free B4C - β-SiC ceramic composites. © 2021 Elsevier Ltd