Rietveld refinement of crystal phases (Ca1-xLax)MnO3 with perovskite-type structure
Abstract
Two nanopowders with nominal compositions (Ca0.7La0.3)MnO3 (CLM) and (Ca0.7La0.3)(Mn0.8Ce0.2)O-3 (CLMC) were synthesized by a modified glycine/nitrate procedure. XRD analysis revealed binary phase mixture in both samples. The influence of La and Ce on unit cell parameters, atom positions, and average bond distances were analyzed. According to these results and refined occupation factors of La and Ca, as well as quantitative phase analysis it was found that the CLM sample consists of 85 mass.% of Ca0.62La0.38MnO3 and 15 mass.% of Ca0.99La0.01MnO3, while the CLMC sample consists of 70 mass.% of Ca0.58La0.42MnO3 and 30 mass.% of CeO2. Microstructure size-strain analysis was performed and the Rietveld refinement gave crystallites of about 100 angstrom. TEM images showed particle sizes of about 100-500 angstrom.
Keywords:
(Ca1-xLax)MnO3 / modified glycine/nitrate procedure / perovskite / quantitative phase analysis / rietveld refinement / SOFCSource:
Materials Science Forum, 2007, 555, 231-+Note:
- Research Trends in Contemporary Materials Science, 8th Conference of the Yugoslav-Materials-Research-Society (Yu-MRS), Sep 04-08, 2006, Herceg Novi, Montenegro
Collections
Institution/Community
VinčaTY - CONF AU - Dukić, Jelena AU - Bošković, Snežana B. AU - Matović, Branko AU - Dimčić, Biljana AU - Karanović, Ljiljana PY - 2007 UR - https://vinar.vin.bg.ac.rs/handle/123456789/6686 AB - Two nanopowders with nominal compositions (Ca0.7La0.3)MnO3 (CLM) and (Ca0.7La0.3)(Mn0.8Ce0.2)O-3 (CLMC) were synthesized by a modified glycine/nitrate procedure. XRD analysis revealed binary phase mixture in both samples. The influence of La and Ce on unit cell parameters, atom positions, and average bond distances were analyzed. According to these results and refined occupation factors of La and Ca, as well as quantitative phase analysis it was found that the CLM sample consists of 85 mass.% of Ca0.62La0.38MnO3 and 15 mass.% of Ca0.99La0.01MnO3, while the CLMC sample consists of 70 mass.% of Ca0.58La0.42MnO3 and 30 mass.% of CeO2. Microstructure size-strain analysis was performed and the Rietveld refinement gave crystallites of about 100 angstrom. TEM images showed particle sizes of about 100-500 angstrom. C3 - Materials Science Forum T1 - Rietveld refinement of crystal phases (Ca1-xLax)MnO3 with perovskite-type structure VL - 555 SP - 231 EP - + DO - 10.4028/www.scientific.net/MSF.555.231 ER -
@conference{ author = "Dukić, Jelena and Bošković, Snežana B. and Matović, Branko and Dimčić, Biljana and Karanović, Ljiljana", year = "2007", abstract = "Two nanopowders with nominal compositions (Ca0.7La0.3)MnO3 (CLM) and (Ca0.7La0.3)(Mn0.8Ce0.2)O-3 (CLMC) were synthesized by a modified glycine/nitrate procedure. XRD analysis revealed binary phase mixture in both samples. The influence of La and Ce on unit cell parameters, atom positions, and average bond distances were analyzed. According to these results and refined occupation factors of La and Ca, as well as quantitative phase analysis it was found that the CLM sample consists of 85 mass.% of Ca0.62La0.38MnO3 and 15 mass.% of Ca0.99La0.01MnO3, while the CLMC sample consists of 70 mass.% of Ca0.58La0.42MnO3 and 30 mass.% of CeO2. Microstructure size-strain analysis was performed and the Rietveld refinement gave crystallites of about 100 angstrom. TEM images showed particle sizes of about 100-500 angstrom.", journal = "Materials Science Forum", title = "Rietveld refinement of crystal phases (Ca1-xLax)MnO3 with perovskite-type structure", volume = "555", pages = "231-+", doi = "10.4028/www.scientific.net/MSF.555.231" }
Dukić, J., Bošković, S. B., Matović, B., Dimčić, B.,& Karanović, L.. (2007). Rietveld refinement of crystal phases (Ca1-xLax)MnO3 with perovskite-type structure. in Materials Science Forum, 555, 231-+. https://doi.org/10.4028/www.scientific.net/MSF.555.231
Dukić J, Bošković SB, Matović B, Dimčić B, Karanović L. Rietveld refinement of crystal phases (Ca1-xLax)MnO3 with perovskite-type structure. in Materials Science Forum. 2007;555:231-+. doi:10.4028/www.scientific.net/MSF.555.231 .
Dukić, Jelena, Bošković, Snežana B., Matović, Branko, Dimčić, Biljana, Karanović, Ljiljana, "Rietveld refinement of crystal phases (Ca1-xLax)MnO3 with perovskite-type structure" in Materials Science Forum, 555 (2007):231-+, https://doi.org/10.4028/www.scientific.net/MSF.555.231 . .