Investigation of the Morphology and Surface Properties of Crosslinked Poly(Urethane-Ester-Siloxane)S
2012
Authors
Džunuzović, Jasna V.Pergal, Marija V.
Vodnik, Vesna
Spirkova, Milena
Poreba, Rafal
Jovanovic, Slobodan
Article
Metadata
Show full item recordAbstract
INVESTIGATION OF THE MORPHOLOGY AND SURFACE PROPERTIES OF CROSSLINKED POLY(URETHANE-ESTER-SILOXANE)S Jasna V. Dzunuzovic(1), Marija V. Pergal(1), Vesna V. Vodnik(2), Milena Spirkova(3), Rafal Poreba(3), Slobodan Jovanovic(4) (1)University of Belgrade, Institute of Chemistry, Technology and Metallurgy (ICTM) Center of Chemistry, Belgrade, Serbia (2)University of Belgrade, Institute of Nuclear Science Vinca, Belgrade, Serbia (3)Institute of Macromolecular Chemistry AS CR, v.v.i., Nanostructured Polymers and Composites Department, Praha, Czech Republic (4)University of Belgrade, Faculty of Technology and Metallurgy, Belgrade, Serbia (Scientific paper) Two series of crosslinked poly(urethane-ester-siloxane)s were synthesized from alpha,omega-dihydroxy-(ethylene oxide-poly(dimethylsiloxane)-ethylene oxide) (EO-PDMS-EO), 4,4-methylenediphenyl diisocyanate and Boltorn (R) hyperbranched polyesters of the second and third pseudo generation, by two-step polymerization in solution. The effect of ...the EO-PDMS-EO content and functionality of the applied crosslinking agent on the morphology and surface properties of the prepared poly(urethane-ester-siloxane)s was investigated by FTIR spectroscopy, small-angle X-ray scattering (SAXS), atomic force microscopy (AFM), scanning electron microscopy (SEM) and water absorption measurement. Different techniques (FTIR peak deconvolution, SAXS and AFM) revealed that decrease of the crosslinking agent functionality and EO-PDMS-EO content promotes microphase separation in the synthesized poly(urethane-ester-siloxane)s. SEM analysis and water absorption experiments showed that, due to the hydrophobic character of EO-PDMS-EO and its ability to migrate to the surface of poly(urethane-ester-siloxane)s, samples synthesized with higher EO-PDMS-EO content and crosslinking agents of lower functionality had more hydrophobic surfaces and better waterproof performances. The obtained results indicate that the synthesis of poly(urethane-ester-siloxane)s based on EO-PDMS-EO and Boltorn (R) hyperbranched polyesters leads to the creation of networks with interesting morphological and surface properties, which can be easily tailored by changing the content of EO-PDMS-EO segment or functionality of hyperbranched polyester.
Keywords:
Hyperbranched polyester / Poly(dimethylsiloxane) / Crosslinked polyurethane / Morphology / Surface propertiesSource:
Hemijska industrija, 2012, 66, 6, 813-821Funding / projects:
- Synthesis and characterization of novel functional polymers and polymeric nanocomposites (RS-MESTD-Basic Research (BR or ON)-172062)
DOI: 10.2298/HEMIND121004101D
ISSN: 0367-598X
WoS: 000315368700003
Scopus: 2-s2.0-84871706465
Collections
Institution/Community
VinčaTY - JOUR AU - Džunuzović, Jasna V. AU - Pergal, Marija V. AU - Vodnik, Vesna AU - Spirkova, Milena AU - Poreba, Rafal AU - Jovanovic, Slobodan PY - 2012 UR - https://vinar.vin.bg.ac.rs/handle/123456789/5338 AB - INVESTIGATION OF THE MORPHOLOGY AND SURFACE PROPERTIES OF CROSSLINKED POLY(URETHANE-ESTER-SILOXANE)S Jasna V. Dzunuzovic(1), Marija V. Pergal(1), Vesna V. Vodnik(2), Milena Spirkova(3), Rafal Poreba(3), Slobodan Jovanovic(4) (1)University of Belgrade, Institute of Chemistry, Technology and Metallurgy (ICTM) Center of Chemistry, Belgrade, Serbia (2)University of Belgrade, Institute of Nuclear Science Vinca, Belgrade, Serbia (3)Institute of Macromolecular Chemistry AS CR, v.v.i., Nanostructured Polymers and Composites Department, Praha, Czech Republic (4)University of Belgrade, Faculty of Technology and Metallurgy, Belgrade, Serbia (Scientific paper) Two series of crosslinked poly(urethane-ester-siloxane)s were synthesized from alpha,omega-dihydroxy-(ethylene oxide-poly(dimethylsiloxane)-ethylene oxide) (EO-PDMS-EO), 4,4-methylenediphenyl diisocyanate and Boltorn (R) hyperbranched polyesters of the second and third pseudo generation, by two-step polymerization in solution. The effect of the EO-PDMS-EO content and functionality of the applied crosslinking agent on the morphology and surface properties of the prepared poly(urethane-ester-siloxane)s was investigated by FTIR spectroscopy, small-angle X-ray scattering (SAXS), atomic force microscopy (AFM), scanning electron microscopy (SEM) and water absorption measurement. Different techniques (FTIR peak deconvolution, SAXS and AFM) revealed that decrease of the crosslinking agent functionality and EO-PDMS-EO content promotes microphase separation in the synthesized poly(urethane-ester-siloxane)s. SEM analysis and water absorption experiments showed that, due to the hydrophobic character of EO-PDMS-EO and its ability to migrate to the surface of poly(urethane-ester-siloxane)s, samples synthesized with higher EO-PDMS-EO content and crosslinking agents of lower functionality had more hydrophobic surfaces and better waterproof performances. The obtained results indicate that the synthesis of poly(urethane-ester-siloxane)s based on EO-PDMS-EO and Boltorn (R) hyperbranched polyesters leads to the creation of networks with interesting morphological and surface properties, which can be easily tailored by changing the content of EO-PDMS-EO segment or functionality of hyperbranched polyester. T2 - Hemijska industrija T1 - Investigation of the Morphology and Surface Properties of Crosslinked Poly(Urethane-Ester-Siloxane)S VL - 66 IS - 6 SP - 813 EP - 821 DO - 10.2298/HEMIND121004101D ER -
@article{ author = "Džunuzović, Jasna V. and Pergal, Marija V. and Vodnik, Vesna and Spirkova, Milena and Poreba, Rafal and Jovanovic, Slobodan", year = "2012", abstract = "INVESTIGATION OF THE MORPHOLOGY AND SURFACE PROPERTIES OF CROSSLINKED POLY(URETHANE-ESTER-SILOXANE)S Jasna V. Dzunuzovic(1), Marija V. Pergal(1), Vesna V. Vodnik(2), Milena Spirkova(3), Rafal Poreba(3), Slobodan Jovanovic(4) (1)University of Belgrade, Institute of Chemistry, Technology and Metallurgy (ICTM) Center of Chemistry, Belgrade, Serbia (2)University of Belgrade, Institute of Nuclear Science Vinca, Belgrade, Serbia (3)Institute of Macromolecular Chemistry AS CR, v.v.i., Nanostructured Polymers and Composites Department, Praha, Czech Republic (4)University of Belgrade, Faculty of Technology and Metallurgy, Belgrade, Serbia (Scientific paper) Two series of crosslinked poly(urethane-ester-siloxane)s were synthesized from alpha,omega-dihydroxy-(ethylene oxide-poly(dimethylsiloxane)-ethylene oxide) (EO-PDMS-EO), 4,4-methylenediphenyl diisocyanate and Boltorn (R) hyperbranched polyesters of the second and third pseudo generation, by two-step polymerization in solution. The effect of the EO-PDMS-EO content and functionality of the applied crosslinking agent on the morphology and surface properties of the prepared poly(urethane-ester-siloxane)s was investigated by FTIR spectroscopy, small-angle X-ray scattering (SAXS), atomic force microscopy (AFM), scanning electron microscopy (SEM) and water absorption measurement. Different techniques (FTIR peak deconvolution, SAXS and AFM) revealed that decrease of the crosslinking agent functionality and EO-PDMS-EO content promotes microphase separation in the synthesized poly(urethane-ester-siloxane)s. SEM analysis and water absorption experiments showed that, due to the hydrophobic character of EO-PDMS-EO and its ability to migrate to the surface of poly(urethane-ester-siloxane)s, samples synthesized with higher EO-PDMS-EO content and crosslinking agents of lower functionality had more hydrophobic surfaces and better waterproof performances. The obtained results indicate that the synthesis of poly(urethane-ester-siloxane)s based on EO-PDMS-EO and Boltorn (R) hyperbranched polyesters leads to the creation of networks with interesting morphological and surface properties, which can be easily tailored by changing the content of EO-PDMS-EO segment or functionality of hyperbranched polyester.", journal = "Hemijska industrija", title = "Investigation of the Morphology and Surface Properties of Crosslinked Poly(Urethane-Ester-Siloxane)S", volume = "66", number = "6", pages = "813-821", doi = "10.2298/HEMIND121004101D" }
Džunuzović, J. V., Pergal, M. V., Vodnik, V., Spirkova, M., Poreba, R.,& Jovanovic, S.. (2012). Investigation of the Morphology and Surface Properties of Crosslinked Poly(Urethane-Ester-Siloxane)S. in Hemijska industrija, 66(6), 813-821. https://doi.org/10.2298/HEMIND121004101D
Džunuzović JV, Pergal MV, Vodnik V, Spirkova M, Poreba R, Jovanovic S. Investigation of the Morphology and Surface Properties of Crosslinked Poly(Urethane-Ester-Siloxane)S. in Hemijska industrija. 2012;66(6):813-821. doi:10.2298/HEMIND121004101D .
Džunuzović, Jasna V., Pergal, Marija V., Vodnik, Vesna, Spirkova, Milena, Poreba, Rafal, Jovanovic, Slobodan, "Investigation of the Morphology and Surface Properties of Crosslinked Poly(Urethane-Ester-Siloxane)S" in Hemijska industrija, 66, no. 6 (2012):813-821, https://doi.org/10.2298/HEMIND121004101D . .