Self-assembled polyaniline nanotubes and nanoribbons/titanium dioxide nanocomposites
Нема приказа
Аутори
Radoičić, Marija B.Šaponjić, Zoran
Nedeljković, Jovan
Ćirić-Marjanović, Gordana N.
Stejskal, Jaroslav
Чланак у часопису
Метаподаци
Приказ свих података о документуАпстракт
Self-assembled polyaniline (PANI) nanotubes, accompanied with nanoribbons, were synthesized by the oxidative polymerization of aniline with ammonium peroxydisulfate in an aqueous medium, in the presence of colloidal titanium dioxide (TiO(2)) nanoparticles of 4.5 nm size, without added acid. The morphology, structure, and physicochemical properties of the PANI/TiO(2) nanocomposites. prepared at various initial aniline/TiO(2) mole ratios, were studied by scanning (SEM) and transmission (TEM) electron microscopies, FTIR, Raman and inductively coupled plasma optical emission (ICP-OES) spectroscopies, elemental analysis, X-ray powder diffraction (XRPD), conductivity measurements, and thermogravimetric analysis (TGA). The electrical conductivity of PANI/TiO(2) nanocomposites increases in the range 3.8 x 10(-4) to 1.1 x 10(-3) S cm(-1) by increasing aniline/TiO(2) mole ratio from 1 to 10. The morphology of PANI/TiO(2) nanocomposites significantly depends on the initial aniline/TiO(2) mole rat...io. In the morphology of the nanocomposite synthesized using aniline/TiO(2) mole ratio 10, nanotubes accompanied with nanosheets prevail. The nanocomposite synthesized at aniline/TiO(2) mole ratio 5 consists of the network of nanotubes (an outer diameter 30-40 nm, an inner diameter 4-7 nm) and nanorods (diameter 50-90 nm), accompanied with nanoribbons (a thickness, width, and length in the range of 50-70 nm, 160-350 nm, and similar to 1-3 mu m, respectively). The PANI/TiO(2) nanocomposite synthesized at aniline/TiO(2) mole ratio 2 contains polyhedral submicrometre particles accompanied with nanotubes, while the nanocomposite prepared at aniline/TiO(2) mole ratio 1 consists of agglomerated nanofibers, submicrometre and nanoparticles. The presence of emeraldine salt form of PANI, linear and branched PANI chains, and phenazine units in PANI/TiO(2) nanocomposites was proved by FTIR and Raman spectroscopies. The improved thermal stability of PANI matrix in all PANI/TiO(2) nanocomposites was observed. (C) 2010 Elsevier B.V. All rights reserved.
Кључне речи:
Nanocomposites / Nanoribbons / Nanostructures / Nanotubes / Polyaniline / Titanium dioxideИзвор:
Synthetic Metals, 2010, 160, 11-12, 1325-1334Финансирање / пројекти:
- Ministry of Science and Technological Development of Serbia [142047, 142066], Czech Grant Agency [202/09/1626]
DOI: 10.1016/j.synthmet.2010.04.010
ISSN: 0379-6779
WoS: 000279625900034
Scopus: 2-s2.0-77953322821
Колекције
Институција/група
VinčaTY - JOUR AU - Radoičić, Marija B. AU - Šaponjić, Zoran AU - Nedeljković, Jovan AU - Ćirić-Marjanović, Gordana N. AU - Stejskal, Jaroslav PY - 2010 UR - https://vinar.vin.bg.ac.rs/handle/123456789/4035 AB - Self-assembled polyaniline (PANI) nanotubes, accompanied with nanoribbons, were synthesized by the oxidative polymerization of aniline with ammonium peroxydisulfate in an aqueous medium, in the presence of colloidal titanium dioxide (TiO(2)) nanoparticles of 4.5 nm size, without added acid. The morphology, structure, and physicochemical properties of the PANI/TiO(2) nanocomposites. prepared at various initial aniline/TiO(2) mole ratios, were studied by scanning (SEM) and transmission (TEM) electron microscopies, FTIR, Raman and inductively coupled plasma optical emission (ICP-OES) spectroscopies, elemental analysis, X-ray powder diffraction (XRPD), conductivity measurements, and thermogravimetric analysis (TGA). The electrical conductivity of PANI/TiO(2) nanocomposites increases in the range 3.8 x 10(-4) to 1.1 x 10(-3) S cm(-1) by increasing aniline/TiO(2) mole ratio from 1 to 10. The morphology of PANI/TiO(2) nanocomposites significantly depends on the initial aniline/TiO(2) mole ratio. In the morphology of the nanocomposite synthesized using aniline/TiO(2) mole ratio 10, nanotubes accompanied with nanosheets prevail. The nanocomposite synthesized at aniline/TiO(2) mole ratio 5 consists of the network of nanotubes (an outer diameter 30-40 nm, an inner diameter 4-7 nm) and nanorods (diameter 50-90 nm), accompanied with nanoribbons (a thickness, width, and length in the range of 50-70 nm, 160-350 nm, and similar to 1-3 mu m, respectively). The PANI/TiO(2) nanocomposite synthesized at aniline/TiO(2) mole ratio 2 contains polyhedral submicrometre particles accompanied with nanotubes, while the nanocomposite prepared at aniline/TiO(2) mole ratio 1 consists of agglomerated nanofibers, submicrometre and nanoparticles. The presence of emeraldine salt form of PANI, linear and branched PANI chains, and phenazine units in PANI/TiO(2) nanocomposites was proved by FTIR and Raman spectroscopies. The improved thermal stability of PANI matrix in all PANI/TiO(2) nanocomposites was observed. (C) 2010 Elsevier B.V. All rights reserved. T2 - Synthetic Metals T1 - Self-assembled polyaniline nanotubes and nanoribbons/titanium dioxide nanocomposites VL - 160 IS - 11-12 SP - 1325 EP - 1334 DO - 10.1016/j.synthmet.2010.04.010 ER -
@article{ author = "Radoičić, Marija B. and Šaponjić, Zoran and Nedeljković, Jovan and Ćirić-Marjanović, Gordana N. and Stejskal, Jaroslav", year = "2010", abstract = "Self-assembled polyaniline (PANI) nanotubes, accompanied with nanoribbons, were synthesized by the oxidative polymerization of aniline with ammonium peroxydisulfate in an aqueous medium, in the presence of colloidal titanium dioxide (TiO(2)) nanoparticles of 4.5 nm size, without added acid. The morphology, structure, and physicochemical properties of the PANI/TiO(2) nanocomposites. prepared at various initial aniline/TiO(2) mole ratios, were studied by scanning (SEM) and transmission (TEM) electron microscopies, FTIR, Raman and inductively coupled plasma optical emission (ICP-OES) spectroscopies, elemental analysis, X-ray powder diffraction (XRPD), conductivity measurements, and thermogravimetric analysis (TGA). The electrical conductivity of PANI/TiO(2) nanocomposites increases in the range 3.8 x 10(-4) to 1.1 x 10(-3) S cm(-1) by increasing aniline/TiO(2) mole ratio from 1 to 10. The morphology of PANI/TiO(2) nanocomposites significantly depends on the initial aniline/TiO(2) mole ratio. In the morphology of the nanocomposite synthesized using aniline/TiO(2) mole ratio 10, nanotubes accompanied with nanosheets prevail. The nanocomposite synthesized at aniline/TiO(2) mole ratio 5 consists of the network of nanotubes (an outer diameter 30-40 nm, an inner diameter 4-7 nm) and nanorods (diameter 50-90 nm), accompanied with nanoribbons (a thickness, width, and length in the range of 50-70 nm, 160-350 nm, and similar to 1-3 mu m, respectively). The PANI/TiO(2) nanocomposite synthesized at aniline/TiO(2) mole ratio 2 contains polyhedral submicrometre particles accompanied with nanotubes, while the nanocomposite prepared at aniline/TiO(2) mole ratio 1 consists of agglomerated nanofibers, submicrometre and nanoparticles. The presence of emeraldine salt form of PANI, linear and branched PANI chains, and phenazine units in PANI/TiO(2) nanocomposites was proved by FTIR and Raman spectroscopies. The improved thermal stability of PANI matrix in all PANI/TiO(2) nanocomposites was observed. (C) 2010 Elsevier B.V. All rights reserved.", journal = "Synthetic Metals", title = "Self-assembled polyaniline nanotubes and nanoribbons/titanium dioxide nanocomposites", volume = "160", number = "11-12", pages = "1325-1334", doi = "10.1016/j.synthmet.2010.04.010" }
Radoičić, M. B., Šaponjić, Z., Nedeljković, J., Ćirić-Marjanović, G. N.,& Stejskal, J.. (2010). Self-assembled polyaniline nanotubes and nanoribbons/titanium dioxide nanocomposites. in Synthetic Metals, 160(11-12), 1325-1334. https://doi.org/10.1016/j.synthmet.2010.04.010
Radoičić MB, Šaponjić Z, Nedeljković J, Ćirić-Marjanović GN, Stejskal J. Self-assembled polyaniline nanotubes and nanoribbons/titanium dioxide nanocomposites. in Synthetic Metals. 2010;160(11-12):1325-1334. doi:10.1016/j.synthmet.2010.04.010 .
Radoičić, Marija B., Šaponjić, Zoran, Nedeljković, Jovan, Ćirić-Marjanović, Gordana N., Stejskal, Jaroslav, "Self-assembled polyaniline nanotubes and nanoribbons/titanium dioxide nanocomposites" in Synthetic Metals, 160, no. 11-12 (2010):1325-1334, https://doi.org/10.1016/j.synthmet.2010.04.010 . .