A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis
Authorized Users Only
2019
Authors
Čolović, Božana M.Janković, Ognjenka
Živković, Slavoljub
Žižak, Željko
Besu Žižak, Irina
Jokanović, Vukoman R.
Article (Published version)
,
© 2019 Elsevier Ltd and Techna Group S.r.l.
Metadata
Show full item recordAbstract
The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice. © 2019 Elsevier Ltd and Techna Group S.r.l.
Keywords:
Calcium aluminate / Powders / Chemical preparation / Strength / Biomedical applicationSource:
Ceramics International, 2019, 45, 7, 9211-9218Funding / projects:
- Chemical and structural designing of nanomaterials for application in medicine and tissue engineering (RS-MESTD-Basic Research (BR or ON)-172026)
DOI: 10.1016/j.ceramint.2019.01.266
ISSN: 0272-8842
WoS: 000463688500142
Scopus: 2-s2.0-85060930006
Collections
Institution/Community
VinčaTY - JOUR AU - Čolović, Božana M. AU - Janković, Ognjenka AU - Živković, Slavoljub AU - Žižak, Željko AU - Besu Žižak, Irina AU - Jokanović, Vukoman R. PY - 2019 UR - https://vinar.vin.bg.ac.rs/handle/123456789/8488 AB - The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice. © 2019 Elsevier Ltd and Techna Group S.r.l. T2 - Ceramics International T1 - A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis VL - 45 IS - 7 SP - 9211 EP - 9218 DO - 10.1016/j.ceramint.2019.01.266 ER -
@article{ author = "Čolović, Božana M. and Janković, Ognjenka and Živković, Slavoljub and Žižak, Željko and Besu Žižak, Irina and Jokanović, Vukoman R.", year = "2019", abstract = "The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice. © 2019 Elsevier Ltd and Techna Group S.r.l.", journal = "Ceramics International", title = "A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis", volume = "45", number = "7", pages = "9211-9218", doi = "10.1016/j.ceramint.2019.01.266" }
Čolović, B. M., Janković, O., Živković, S., Žižak, Ž., Besu Žižak, I.,& Jokanović, V. R.. (2019). A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis. in Ceramics International, 45(7), 9211-9218. https://doi.org/10.1016/j.ceramint.2019.01.266
Čolović BM, Janković O, Živković S, Žižak Ž, Besu Žižak I, Jokanović VR. A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis. in Ceramics International. 2019;45(7):9211-9218. doi:10.1016/j.ceramint.2019.01.266 .
Čolović, Božana M., Janković, Ognjenka, Živković, Slavoljub, Žižak, Željko, Besu Žižak, Irina, Jokanović, Vukoman R., "A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis" in Ceramics International, 45, no. 7 (2019):9211-9218, https://doi.org/10.1016/j.ceramint.2019.01.266 . .