Structural, morphological and electrical properties of multi-doped calcium phosphate materials as solid electrolytes for intermediate temperature solid oxide fuel cells
(Science of Sintering, 2018)
Modified solution precipitation method was used to prepare pure and doped Mg, Sr and Na hydroxyapatite type materials (CaP, CaMgP and CaSrNaP). Modification consisted of partial substitution of nitrates by acetate solution ...
Structure and photocatalytic properties of sintered TiO2 nanotube arrays
(Science of Sintering, 2018)
One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...
Use of sintering to immobilize toxic metals present in galvanic sludge into a stabile glass-ceramic structure
(Science of Sintering, 2018)
Galvanization process requires the use a large amount of water and produces wastewaters that are usually purified by conventional cost-effective procedure. This kind of treatment generates waste sludge which becomes a ...
Macroporous monoliths based оn natural mineral sources, clay аnd diatomite
(Science of Sintering, 2020)
Macroporous silica ceramic was obtained using clay and diatomite. Boric acid as a low-cost additive in the amount of 1 wt% was used. These porous materials were obtained at low forming pressure (40-80 MPa) and lower sintering ...
Effect of Milling Time on Mechanical Properties of Anorthite Obtained by Thermal Transformation of Ca-LTA Zeolite
(Science of Sintering, 2022)
Anorthite ceramics was fabricated from calcium exchanged Na-LTA zeolite. The powder compacts of Ca-LTA zeolite were sintered at different temperatures ranging between 1100 and 1400°C. It was found that the temperature of ...
Application of the final flotation waste for obtaining the glass-ceramic materials
(Science of Sintering, 2017)
This work describes the investigation of the final flotation waste (FFW), originating from the RTB Bor Company (Serbia), as the main component for the production of glass-ceramic materials. The glass-ceramics was synthesized ...
Influence of grinding, pressing and sintering of the powder 50.0 wt% Fe, 47.0 wt% BaTiO3 and 3.0 wt% TiO2 on morphology, microstructure, magnetic and electric properties
(Science of Sintering, 2023)
A mixture of 50.0 wt% Fe, 47.0 wt% BaTiO3, and 3.0 wt% TiO2 powders is milled and then pressed and sintered. Samples sintered from ground powders have a structure consisting of plates. They consist of the crystalline phase ...