Primena plazme indukovane TEA CO2 laserskim zračenjem za određivanje koncentracije magnezijuma u aluminijumskim legurama

Abstract

Ispitivana je mogućnost analitičke primene plazme indukovane nanosekundnim infracrvenim TEA CO2 laserskim zračenjem za određivanje koncentracije Mg u aluminijumskim legurama, pri sniženom pritisku vazduha. Oštre i dobro razložene spektralne linije Mg, uz nisku emisiju pozadine, dobijene su posmatranjem plazme na rastojanju 3 mm od površine mete. Kalibraciona kriva za Mg konstruisana je korišćenjem sertifikovanih uzoraka aluminijumskih legura. Dobijena je linearna zavisnost između LIBS signala i koncentracije analita (r2=0,9957) u opsegu od 0,26-1,10 % m/m i korišćena je za određivanje koncetracije Mg u kontrolnom uzorku. Kao referentna metoda za kvantifikovanje Mg u kontrolnom uzorku korišćena je induktivno spregnuta plazma - optičko emisiona spektroskopija (ICP-OES). Dobijeno je odlično slaganje između LIBS i ICP-OES rezultata. Rezultati potvrđuju da je TEA CO2 LIBS efikasna tehnika za kvantitativnu analizu Mg u uzorcima aluminijumskih legura.

The analytical capability of plasma induced by nanosecond infrared TEA CO2 laser radiation under reduced air pressure for determination of Mg in aluminum alloys was investigated. Sharp and well resolved spectral lines of Mg, with negligibly low background emission, were obtained from a plasma region 3 mm above the target surface. A calibration curve for Mg was constructed using certified aluminium alloy samples. A linear relationship between LIBS signal and analyte concentration was obtained (r2 = 0.9957) ) in the range from 0,26 -1,10 % w/w, and used for determination of Mg in a control sample. As a reference method for quantification of Mg in the control sample inductively coupled plasma - optical emission spectroscopy (ICP-OES) was used. Good agreement between LIBS and ICP-OES results was obtained. The results confirm that TEA CO2 LIBS is an effective technique for quantitative analysis of Mg in aluminum alloy samples.