AB  - The behavior of 16Cr3Al ODS steel (oxide dispersion strengthened steel), widely employed structural fusion material, under high-intensity laser radiation with intensity up to 10(14)W/cm(2) was investigated in air, helium and vacuum surrounding. Employed system was 65 fs laser at 804 nm, with applied pulse energy up to 5.25 mJ. Morphological effects were studied - cracking, crater parameters (depth, cross-section), LIPSS (laser-induced periodic surface structures) formation at the crater periphery, hydrodynamic effects, as well as chemical variations on the surface. Ablation thresholds were also determined for all three ambiences (for 100 applied pulses), and they were 0.30 J/cm(2), 0.23 J/cm(2) and 0.39 J/cm(2) in air, helium and vacuum, respectively. Plasma occurred in all experiments and it was most prominent in vacuum due to strongest laser-material coupling.
T2  - Fusion Engineering and Design
T1  - Surface behavior of 16Cr3Al ODS steel—Effects of high laser intensity 1014 W/cm2 in ambiences of air, helium and vacuum
VL  - 150
SP  - 111360
DO  - 10.1016/j.fusengdes.2019.111360
ER  - 

@article{
author = "Trtica, Milan and Stašić, Jelena and Limpouch, Jiri and Gavrilov, Peter T. and Chen, X. and Ciganović, Jovan",
year = "2020",
abstract = "The behavior of 16Cr3Al ODS steel (oxide dispersion strengthened steel), widely employed structural fusion material, under high-intensity laser radiation with intensity up to 10(14)W/cm(2) was investigated in air, helium and vacuum surrounding. Employed system was 65 fs laser at 804 nm, with applied pulse energy up to 5.25 mJ. Morphological effects were studied - cracking, crater parameters (depth, cross-section), LIPSS (laser-induced periodic surface structures) formation at the crater periphery, hydrodynamic effects, as well as chemical variations on the surface. Ablation thresholds were also determined for all three ambiences (for 100 applied pulses), and they were 0.30 J/cm(2), 0.23 J/cm(2) and 0.39 J/cm(2) in air, helium and vacuum, respectively. Plasma occurred in all experiments and it was most prominent in vacuum due to strongest laser-material coupling.",
journal = "Fusion Engineering and Design",
title = "Surface behavior of 16Cr3Al ODS steel—Effects of high laser intensity 1014 W/cm2 in ambiences of air, helium and vacuum",
volume = "150",
pages = "111360",
doi = "10.1016/j.fusengdes.2019.111360"
}

Trtica, M., Stašić, J., Limpouch, J., Gavrilov, P. T., Chen, X.,& Ciganović, J.. (2020). Surface behavior of 16Cr3Al ODS steel—Effects of high laser intensity 1014 W/cm2 in ambiences of air, helium and vacuum. in Fusion Engineering and Design, 150, 111360.
https://doi.org/10.1016/j.fusengdes.2019.111360

Trtica M, Stašić J, Limpouch J, Gavrilov PT, Chen X, Ciganović J. Surface behavior of 16Cr3Al ODS steel—Effects of high laser intensity 1014 W/cm2 in ambiences of air, helium and vacuum. in Fusion Engineering and Design. 2020;150:111360.
doi:10.1016/j.fusengdes.2019.111360 .

Trtica, Milan, Stašić, Jelena, Limpouch, Jiri, Gavrilov, Peter T., Chen, X., Ciganović, Jovan, "Surface behavior of 16Cr3Al ODS steel—Effects of high laser intensity 1014 W/cm2 in ambiences of air, helium and vacuum" in Fusion Engineering and Design, 150 (2020):111360,
https://doi.org/10.1016/j.fusengdes.2019.111360 . .