TY  - JOUR
AU  - Dinić, Ivana
AU  - Vuković, Marina
AU  - Rabanal, Maria Eugenia
AU  - Milošević, Milica
AU  - Bukumira, Marta
AU  - Tomić, Nina
AU  - Tomić, Miloš
AU  - Mančić, Lidija
AU  - Ignjatović, Nenad
PY  - 2024
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/12299
AB  - Y0.8−xGdxF3 :Yb/Er mesocrystals with a biocompatible surface and diverse morphological characteristics were successfully synthesized using chitosan-assisted solvothermal processing. Their structural properties, studied using X-ray powder diffraction, Fourier transform infrared spectroscopy, scanning and transmission electron microscopy and energy dispersive X-ray analysis, were further correlated with the up-conversion emission (λexc = 976 nm) recorded in function of temperature. Based on the change in the visible green emissions originating from the thermally coupled 2H11/2 and 4S3/2 levels of Er3+, the corresponding LIR was acquired in the physiologically relevant range of temperatures (25–50 ◦C). The detected absolute sensitivity of about 0.0042 ◦C −1 , along with the low cytotoxicity toward both normal human lung fibroblasts (MRC-5) and cancerous lung epithelial (A549) cells, indicate a potential for use in temperature sensing in biomedicine. Additionally, their enhanced internalization in cells, without suppression of cell viability, enabled in vitro labeling of cancer and healthy cells upon 976 nm laser irradiation.
T2  - Journal of Functional Biomaterials
T1  - Temperature Sensing Properties of Biocompatible Yb/Er-Doped GdF3 and YF3 Mesocrystals
VL  - 15
IS  - 1
SP  - 6
DO  - 10.3390/jfb15010006
ER  - 

@article{
author = "Dinić, Ivana and Vuković, Marina and Rabanal, Maria Eugenia and Milošević, Milica and Bukumira, Marta and Tomić, Nina and Tomić, Miloš and Mančić, Lidija and Ignjatović, Nenad",
year = "2024",
abstract = "Y0.8−xGdxF3 :Yb/Er mesocrystals with a biocompatible surface and diverse morphological characteristics were successfully synthesized using chitosan-assisted solvothermal processing. Their structural properties, studied using X-ray powder diffraction, Fourier transform infrared spectroscopy, scanning and transmission electron microscopy and energy dispersive X-ray analysis, were further correlated with the up-conversion emission (λexc = 976 nm) recorded in function of temperature. Based on the change in the visible green emissions originating from the thermally coupled 2H11/2 and 4S3/2 levels of Er3+, the corresponding LIR was acquired in the physiologically relevant range of temperatures (25–50 ◦C). The detected absolute sensitivity of about 0.0042 ◦C −1 , along with the low cytotoxicity toward both normal human lung fibroblasts (MRC-5) and cancerous lung epithelial (A549) cells, indicate a potential for use in temperature sensing in biomedicine. Additionally, their enhanced internalization in cells, without suppression of cell viability, enabled in vitro labeling of cancer and healthy cells upon 976 nm laser irradiation.",
journal = "Journal of Functional Biomaterials",
title = "Temperature Sensing Properties of Biocompatible Yb/Er-Doped GdF3 and YF3 Mesocrystals",
volume = "15",
number = "1",
pages = "6",
doi = "10.3390/jfb15010006"
}

Dinić, I., Vuković, M., Rabanal, M. E., Milošević, M., Bukumira, M., Tomić, N., Tomić, M., Mančić, L.,& Ignjatović, N.. (2024). Temperature Sensing Properties of Biocompatible Yb/Er-Doped GdF3 and YF3 Mesocrystals. in Journal of Functional Biomaterials, 15(1), 6.
https://doi.org/10.3390/jfb15010006

Dinić I, Vuković M, Rabanal ME, Milošević M, Bukumira M, Tomić N, Tomić M, Mančić L, Ignjatović N. Temperature Sensing Properties of Biocompatible Yb/Er-Doped GdF3 and YF3 Mesocrystals. in Journal of Functional Biomaterials. 2024;15(1):6.
doi:10.3390/jfb15010006 .

Dinić, Ivana, Vuković, Marina, Rabanal, Maria Eugenia, Milošević, Milica, Bukumira, Marta, Tomić, Nina, Tomić, Miloš, Mančić, Lidija, Ignjatović, Nenad, "Temperature Sensing Properties of Biocompatible Yb/Er-Doped GdF3 and YF3 Mesocrystals" in Journal of Functional Biomaterials, 15, no. 1 (2024):6,
https://doi.org/10.3390/jfb15010006 . .

TY  - JOUR
AU  - Stamenković, Tijana
AU  - Dinić, Ivana
AU  - Vuković, Marina
AU  - Radmilović, Nadežda
AU  - Barudžija, Tanja
AU  - Tomić, Miloš
AU  - Mančić, Lidija
AU  - Lojpur, Vesna
PY  - 2023
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/11579
AB  - In this investigation, samples of strontium-gadolinium-oxide (SrGd2O4) doped with different Yb3+ (2, 4 and 6 at%) and constant Ho3+ (1 at%) contents and co-doped with Bi3+ (2 at%) were prepared using the glycine-assisted sol–gel method. The pure orthorhombic SrGd2O4 phase, space group Pnma, was revealed using X-ray diffraction in all samples. Transmission electron microscopy discovered agglomerated clusters of spherical particles measuring approximately 150 nm in size. The inclusion of Bi3+ ions into the structure influenced the morphology since the formation of larger grains was observed, with sizes reaching up to ∼1.7 μm. The uniform distribution of all constitutive elements was confirmed by energy-dispersive X-ray spectroscopy. In all samples, up-conversion emission spectra revealed two dominant green (540 and 550 nm), red (671 nm), and infrared (758 nm) emission lines, due to the 5F4,5S2→5I8, 5F5→5I8, and 5F4,5S2 → 5I7 transitions, respectively. The sample co-doped with Bi3+ showed the most intense photoluminescent emissions, shorter luminescence decay, and the highest quantum yield. Additionally, a significant decrease in the energy band gap value was detected using diffuse reflectance spectroscopy for this sample. Methylene blue was used as a test pollutant to investigate its photocatalytic efficiency under simulated sunlight irradiation. The results show that Bi3+ co-doping deteriorates the photocatalytic efficiency of the SrGd2O4:Yb3+/Ho3+ phase by reducing hydroxyl radical formation.
T2  - Ceramics International
T1  - Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase
DO  - 10.1016/j.ceramint.2023.09.103
ER  - 

@article{
author = "Stamenković, Tijana and Dinić, Ivana and Vuković, Marina and Radmilović, Nadežda and Barudžija, Tanja and Tomić, Miloš and Mančić, Lidija and Lojpur, Vesna",
year = "2023",
abstract = "In this investigation, samples of strontium-gadolinium-oxide (SrGd2O4) doped with different Yb3+ (2, 4 and 6 at%) and constant Ho3+ (1 at%) contents and co-doped with Bi3+ (2 at%) were prepared using the glycine-assisted sol–gel method. The pure orthorhombic SrGd2O4 phase, space group Pnma, was revealed using X-ray diffraction in all samples. Transmission electron microscopy discovered agglomerated clusters of spherical particles measuring approximately 150 nm in size. The inclusion of Bi3+ ions into the structure influenced the morphology since the formation of larger grains was observed, with sizes reaching up to ∼1.7 μm. The uniform distribution of all constitutive elements was confirmed by energy-dispersive X-ray spectroscopy. In all samples, up-conversion emission spectra revealed two dominant green (540 and 550 nm), red (671 nm), and infrared (758 nm) emission lines, due to the 5F4,5S2→5I8, 5F5→5I8, and 5F4,5S2 → 5I7 transitions, respectively. The sample co-doped with Bi3+ showed the most intense photoluminescent emissions, shorter luminescence decay, and the highest quantum yield. Additionally, a significant decrease in the energy band gap value was detected using diffuse reflectance spectroscopy for this sample. Methylene blue was used as a test pollutant to investigate its photocatalytic efficiency under simulated sunlight irradiation. The results show that Bi3+ co-doping deteriorates the photocatalytic efficiency of the SrGd2O4:Yb3+/Ho3+ phase by reducing hydroxyl radical formation.",
journal = "Ceramics International",
title = "Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase",
doi = "10.1016/j.ceramint.2023.09.103"
}

Stamenković, T., Dinić, I., Vuković, M., Radmilović, N., Barudžija, T., Tomić, M., Mančić, L.,& Lojpur, V.. (2023). Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase. in Ceramics International.
https://doi.org/10.1016/j.ceramint.2023.09.103

Stamenković T, Dinić I, Vuković M, Radmilović N, Barudžija T, Tomić M, Mančić L, Lojpur V. Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase. in Ceramics International. 2023;.
doi:10.1016/j.ceramint.2023.09.103 .

Stamenković, Tijana, Dinić, Ivana, Vuković, Marina, Radmilović, Nadežda, Barudžija, Tanja, Tomić, Miloš, Mančić, Lidija, Lojpur, Vesna, "Effect of Bi3+co-doping on the up-converting and photocatalytic properties of SrGd2O4:Yb3+/Ho3+ phase" in Ceramics International (2023),
https://doi.org/10.1016/j.ceramint.2023.09.103 . .