TY  - JOUR
AU  - Perić, Dejan
AU  - Ružić, Jovana
AU  - Lević, Steva
AU  - Stašić, Jovana N.
PY  - 2022
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/10418
AB  - Introduction/Objective. The objective was to determine the degree of conversion (DC), cross-link density, percentage of leachable monomers, flexural strength (FS), and hardness (HV) of nanohybrid, nanofilled bulk-fill, giomer, fiber-reinforced, and low-shrinkage composites. Methods. Standardized specimens (n = 5/group) of Tetric EvoCeram Bulk Fill, Filtek Bulk Fill, Beautifil, EverX posterior, Kalore, Filtek Z250 (microhybrid control), and Tetric EvoCeram (nanohybrid control) were subjected to micro-Raman spectroscopy, three-point bending, and HV. Cross-linking density and leachable monomers were ascertained based on the ratio of HV and DC before and after immersion in absolute ethanol. Results. DC was in the range 50.4–70.5%, the highest for Filtek Bulk and the lowest for Kalore. The highest %DC change was in Beautifil (10.3%) and the lowest in Filtek Bulk (1.4%) and Z250 (1.28%). FS ranged between 78.9 MPa (TEC) and 126.7 MPa (Filtek Bulk). HV ranged between 58.6 (Kalore) and 113.9 (Z250) and significantly decreased post-immersion (19–55%). HV48h inversely correlated to HV% loss (r = -0.761), whilst DC positively correlated with FS (r = 0.893). Conclusion. Filtek Bulk, EverX, and Z250 showed the highest DC. The lowest DC and mechanical properties were observed for Kalore. The greatest cross-link density was shown by Filtek Bulk. There were up to 10% of leachable monomers. DC and FS positively correlated.
T2  - Srpski arhiv za celokupno lekarstvo
T1  - Polymer characteristics and mechanical properties of bulk-fill, giomer, fiber-reinforced and low-shrinkage composites
VL  - 150
IS  - 7-8
SP  - 414
EP  - 420
DO  - 10.2298/SARH220129055P
ER  - 

@article{
author = "Perić, Dejan and Ružić, Jovana and Lević, Steva and Stašić, Jovana N.",
year = "2022",
abstract = "Introduction/Objective. The objective was to determine the degree of conversion (DC), cross-link density, percentage of leachable monomers, flexural strength (FS), and hardness (HV) of nanohybrid, nanofilled bulk-fill, giomer, fiber-reinforced, and low-shrinkage composites. Methods. Standardized specimens (n = 5/group) of Tetric EvoCeram Bulk Fill, Filtek Bulk Fill, Beautifil, EverX posterior, Kalore, Filtek Z250 (microhybrid control), and Tetric EvoCeram (nanohybrid control) were subjected to micro-Raman spectroscopy, three-point bending, and HV. Cross-linking density and leachable monomers were ascertained based on the ratio of HV and DC before and after immersion in absolute ethanol. Results. DC was in the range 50.4–70.5%, the highest for Filtek Bulk and the lowest for Kalore. The highest %DC change was in Beautifil (10.3%) and the lowest in Filtek Bulk (1.4%) and Z250 (1.28%). FS ranged between 78.9 MPa (TEC) and 126.7 MPa (Filtek Bulk). HV ranged between 58.6 (Kalore) and 113.9 (Z250) and significantly decreased post-immersion (19–55%). HV48h inversely correlated to HV% loss (r = -0.761), whilst DC positively correlated with FS (r = 0.893). Conclusion. Filtek Bulk, EverX, and Z250 showed the highest DC. The lowest DC and mechanical properties were observed for Kalore. The greatest cross-link density was shown by Filtek Bulk. There were up to 10% of leachable monomers. DC and FS positively correlated.",
journal = "Srpski arhiv za celokupno lekarstvo",
title = "Polymer characteristics and mechanical properties of bulk-fill, giomer, fiber-reinforced and low-shrinkage composites",
volume = "150",
number = "7-8",
pages = "414-420",
doi = "10.2298/SARH220129055P"
}

Perić, D., Ružić, J., Lević, S.,& Stašić, J. N.. (2022). Polymer characteristics and mechanical properties of bulk-fill, giomer, fiber-reinforced and low-shrinkage composites. in Srpski arhiv za celokupno lekarstvo, 150(7-8), 414-420.
https://doi.org/10.2298/SARH220129055P

Perić D, Ružić J, Lević S, Stašić JN. Polymer characteristics and mechanical properties of bulk-fill, giomer, fiber-reinforced and low-shrinkage composites. in Srpski arhiv za celokupno lekarstvo. 2022;150(7-8):414-420.
doi:10.2298/SARH220129055P .

Perić, Dejan, Ružić, Jovana, Lević, Steva, Stašić, Jovana N., "Polymer characteristics and mechanical properties of bulk-fill, giomer, fiber-reinforced and low-shrinkage composites" in Srpski arhiv za celokupno lekarstvo, 150, no. 7-8 (2022):414-420,
https://doi.org/10.2298/SARH220129055P . .

TY  - JOUR
AU  - Miletić, Vesna
AU  - Perić, Dejan
AU  - Milošević, Miloš
AU  - Manojlović, Dragica
AU  - Mitrović, Nenad
PY  - 2016
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/1335
AB  - Objective. To compare strain and displacement of sculptable bulk-fill, low-shrinkage and conventional composites as well as dye penetration along the dentin-restoration interface. Methods. Modified Class II cavities (N= 5/group) were filled with sculptable bulk-fill (Filtek Bulk Fill Posterior, 3M ESPE; Tetric EvoCeram Bulk Fill, Ivoclar Vivadent; fiber-reinforced EverX Posterior, GC; giomer Beautifil Bulk, Schofu), low-shrinkage (Kalore, GC), nanohybrid (Tetric EvoCeram, Ivoclar Vivadent) or microhybrid (Filtek Z250, 3M ESPE) composites. Strain and displacement were determined using the 3D digital image correlation method based on two cameras with 1 mu m displacement sensitivity and 1600 x 1200 pixel resolution (Aramis, GOM). Microleakage along dentin axial and gingival cavity walls was measured under a stereomicroscope using a different set of teeth (N = 8/group). Data were analyzed using analyses of variance with Tukeys post-test, Pearson correlation and paired t-test (alpha = 0.05). Results. Strain of TEC Bulk, Filtek Bulk, Beautifil Bulk and Kalore was in the range of 1-1.5%. EverX and control composites showed 1.5-2% strain. Axial displacements were between 5 mu m and 30 mu m The least strain was identified at 2 mm below the occlusal surface in 4-mm but not in 2-mm layered composites. Greater microleakage occurred along the gingival than axial wall (p LT 0.05). No correlation was found between strain/displacements and microleakage axially (r(2) = 0.082, p = 0.821; r(2) =-0.2, p = 0.605, respectively) or gingivally (r(2) =-0.126, p = 0.729, r(2) =-0.278, p = 0.469, respectively). Significance. Strain i.e. volumetric shrinkage of sculptable bulk-fill and low-shrinkage composites was comparable to control composites but strain distribution across restoration depth differed. Marginal integrity was more compromised along the gingival than axial dentin wall. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
T2  - Dental Materials
T1  - Local deformation fields and marginal integrity of sculptable bulk-fill, low-shrinkage and conventional composites
VL  - 32
IS  - 11
SP  - 1441
EP  - 1451
DO  - 10.1016/j.dental.2016.09.011
ER  - 

@article{
author = "Miletić, Vesna and Perić, Dejan and Milošević, Miloš and Manojlović, Dragica and Mitrović, Nenad",
year = "2016",
abstract = "Objective. To compare strain and displacement of sculptable bulk-fill, low-shrinkage and conventional composites as well as dye penetration along the dentin-restoration interface. Methods. Modified Class II cavities (N= 5/group) were filled with sculptable bulk-fill (Filtek Bulk Fill Posterior, 3M ESPE; Tetric EvoCeram Bulk Fill, Ivoclar Vivadent; fiber-reinforced EverX Posterior, GC; giomer Beautifil Bulk, Schofu), low-shrinkage (Kalore, GC), nanohybrid (Tetric EvoCeram, Ivoclar Vivadent) or microhybrid (Filtek Z250, 3M ESPE) composites. Strain and displacement were determined using the 3D digital image correlation method based on two cameras with 1 mu m displacement sensitivity and 1600 x 1200 pixel resolution (Aramis, GOM). Microleakage along dentin axial and gingival cavity walls was measured under a stereomicroscope using a different set of teeth (N = 8/group). Data were analyzed using analyses of variance with Tukeys post-test, Pearson correlation and paired t-test (alpha = 0.05). Results. Strain of TEC Bulk, Filtek Bulk, Beautifil Bulk and Kalore was in the range of 1-1.5%. EverX and control composites showed 1.5-2% strain. Axial displacements were between 5 mu m and 30 mu m The least strain was identified at 2 mm below the occlusal surface in 4-mm but not in 2-mm layered composites. Greater microleakage occurred along the gingival than axial wall (p LT 0.05). No correlation was found between strain/displacements and microleakage axially (r(2) = 0.082, p = 0.821; r(2) =-0.2, p = 0.605, respectively) or gingivally (r(2) =-0.126, p = 0.729, r(2) =-0.278, p = 0.469, respectively). Significance. Strain i.e. volumetric shrinkage of sculptable bulk-fill and low-shrinkage composites was comparable to control composites but strain distribution across restoration depth differed. Marginal integrity was more compromised along the gingival than axial dentin wall. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.",
journal = "Dental Materials",
title = "Local deformation fields and marginal integrity of sculptable bulk-fill, low-shrinkage and conventional composites",
volume = "32",
number = "11",
pages = "1441-1451",
doi = "10.1016/j.dental.2016.09.011"
}

Miletić, V., Perić, D., Milošević, M., Manojlović, D.,& Mitrović, N.. (2016). Local deformation fields and marginal integrity of sculptable bulk-fill, low-shrinkage and conventional composites. in Dental Materials, 32(11), 1441-1451.
https://doi.org/10.1016/j.dental.2016.09.011

Miletić V, Perić D, Milošević M, Manojlović D, Mitrović N. Local deformation fields and marginal integrity of sculptable bulk-fill, low-shrinkage and conventional composites. in Dental Materials. 2016;32(11):1441-1451.
doi:10.1016/j.dental.2016.09.011 .

Miletić, Vesna, Perić, Dejan, Milošević, Miloš, Manojlović, Dragica, Mitrović, Nenad, "Local deformation fields and marginal integrity of sculptable bulk-fill, low-shrinkage and conventional composites" in Dental Materials, 32, no. 11 (2016):1441-1451,
https://doi.org/10.1016/j.dental.2016.09.011 . .