TY  - JOUR
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Marković, Smilja
AU  - Mitrić, Miodrag
AU  - Balać, Igor
AU  - Đorđević, Antonije
AU  - Pavlović, Vladimir B.
PY  - 2019
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/8441
AB  - Alumina-based compounds have many technological applications and attract great attention even after decades of investigation, due to their good chemical, electrical, and mechanical properties. A mixture of several alumina modifications (α-, κ-, γ-Al2O3) doped with 1 wt% of Mn2O3 was used for this experiment. The powder was mechanically activated for 60 min in an ethanol medium. After compaction, green bodies were sintered in the temperature range from 1200 to 1400 °C. Microstructures of the obtained specimens were investigated by scanning electron microscopy (SEM) and Energy-dispersive X-ray spectroscopy (EDS). The influence of morphological changes on electrical and mechanical properties was examined in detail. We have developed a test fixture and corresponding software for measurement of the relative dielectric permittivity and the loss tangent of ceramic specimens. This new method overcomes the problems of dimensions and shape of samples, as well as the problem of applying silver paste. The accuracy is around 2% for ε'r and 0.003 for tanδ. We demonstrate that the mechanical activation (MA) has the dominant influence on lowering the characteristic temperatures and microstructure development, which further leads to increased permittivity and tensile strength.
T2  - Advanced Powder Technology
T1  - The effect of ball milling on properties of sintered manganese-doped alumina
VL  - 30
IS  - 11
SP  - 2533
EP  - 2540
DO  - 10.1016/j.apt.2019.07.033
ER  - 

@article{
author = "Filipović, Suzana and Obradović, Nina and Marković, Smilja and Mitrić, Miodrag and Balać, Igor and Đorđević, Antonije and Pavlović, Vladimir B.",
year = "2019",
abstract = "Alumina-based compounds have many technological applications and attract great attention even after decades of investigation, due to their good chemical, electrical, and mechanical properties. A mixture of several alumina modifications (α-, κ-, γ-Al2O3) doped with 1 wt% of Mn2O3 was used for this experiment. The powder was mechanically activated for 60 min in an ethanol medium. After compaction, green bodies were sintered in the temperature range from 1200 to 1400 °C. Microstructures of the obtained specimens were investigated by scanning electron microscopy (SEM) and Energy-dispersive X-ray spectroscopy (EDS). The influence of morphological changes on electrical and mechanical properties was examined in detail. We have developed a test fixture and corresponding software for measurement of the relative dielectric permittivity and the loss tangent of ceramic specimens. This new method overcomes the problems of dimensions and shape of samples, as well as the problem of applying silver paste. The accuracy is around 2% for ε'r and 0.003 for tanδ. We demonstrate that the mechanical activation (MA) has the dominant influence on lowering the characteristic temperatures and microstructure development, which further leads to increased permittivity and tensile strength.",
journal = "Advanced Powder Technology",
title = "The effect of ball milling on properties of sintered manganese-doped alumina",
volume = "30",
number = "11",
pages = "2533-2540",
doi = "10.1016/j.apt.2019.07.033"
}

Filipović, S., Obradović, N., Marković, S., Mitrić, M., Balać, I., Đorđević, A.,& Pavlović, V. B.. (2019). The effect of ball milling on properties of sintered manganese-doped alumina. in Advanced Powder Technology, 30(11), 2533-2540.
https://doi.org/10.1016/j.apt.2019.07.033

Filipović S, Obradović N, Marković S, Mitrić M, Balać I, Đorđević A, Pavlović VB. The effect of ball milling on properties of sintered manganese-doped alumina. in Advanced Powder Technology. 2019;30(11):2533-2540.
doi:10.1016/j.apt.2019.07.033 .

Filipović, Suzana, Obradović, Nina, Marković, Smilja, Mitrić, Miodrag, Balać, Igor, Đorđević, Antonije, Pavlović, Vladimir B., "The effect of ball milling on properties of sintered manganese-doped alumina" in Advanced Powder Technology, 30, no. 11 (2019):2533-2540,
https://doi.org/10.1016/j.apt.2019.07.033 . .

TY  - JOUR
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Marković, Smilja
AU  - Mitrić, Miodrag
AU  - Balać, Igor
AU  - Đorđević, Antonije
AU  - Pavlović, Vladimir B.
PY  - 2019
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/8442
AB  - Alumina-based compounds have many technological applications and attract great attention even after decades of investigation, due to their good chemical, electrical, and mechanical properties. A mixture of several alumina modifications (α-, κ-, γ-Al2O3) doped with 1 wt% of Mn2O3 was used for this experiment. The powder was mechanically activated for 60 min in an ethanol medium. After compaction, green bodies were sintered in the temperature range from 1200 to 1400 °C. Microstructures of the obtained specimens were investigated by scanning electron microscopy (SEM) and Energy-dispersive X-ray spectroscopy (EDS). The influence of morphological changes on electrical and mechanical properties was examined in detail. We have developed a test fixture and corresponding software for measurement of the relative dielectric permittivity and the loss tangent of ceramic specimens. This new method overcomes the problems of dimensions and shape of samples, as well as the problem of applying silver paste. The accuracy is around 2% for ε'r and 0.003 for tanδ. We demonstrate that the mechanical activation (MA) has the dominant influence on lowering the characteristic temperatures and microstructure development, which further leads to increased permittivity and tensile strength.
T2  - Advanced Powder Technology
T1  - The effect of ball milling on properties of sintered manganese-doped alumina
VL  - 30
IS  - 11
SP  - 2533
EP  - 2540
DO  - 10.1016/j.apt.2019.07.033
ER  - 

@article{
author = "Filipović, Suzana and Obradović, Nina and Marković, Smilja and Mitrić, Miodrag and Balać, Igor and Đorđević, Antonije and Pavlović, Vladimir B.",
year = "2019",
abstract = "Alumina-based compounds have many technological applications and attract great attention even after decades of investigation, due to their good chemical, electrical, and mechanical properties. A mixture of several alumina modifications (α-, κ-, γ-Al2O3) doped with 1 wt% of Mn2O3 was used for this experiment. The powder was mechanically activated for 60 min in an ethanol medium. After compaction, green bodies were sintered in the temperature range from 1200 to 1400 °C. Microstructures of the obtained specimens were investigated by scanning electron microscopy (SEM) and Energy-dispersive X-ray spectroscopy (EDS). The influence of morphological changes on electrical and mechanical properties was examined in detail. We have developed a test fixture and corresponding software for measurement of the relative dielectric permittivity and the loss tangent of ceramic specimens. This new method overcomes the problems of dimensions and shape of samples, as well as the problem of applying silver paste. The accuracy is around 2% for ε'r and 0.003 for tanδ. We demonstrate that the mechanical activation (MA) has the dominant influence on lowering the characteristic temperatures and microstructure development, which further leads to increased permittivity and tensile strength.",
journal = "Advanced Powder Technology",
title = "The effect of ball milling on properties of sintered manganese-doped alumina",
volume = "30",
number = "11",
pages = "2533-2540",
doi = "10.1016/j.apt.2019.07.033"
}

Filipović, S., Obradović, N., Marković, S., Mitrić, M., Balać, I., Đorđević, A.,& Pavlović, V. B.. (2019). The effect of ball milling on properties of sintered manganese-doped alumina. in Advanced Powder Technology, 30(11), 2533-2540.
https://doi.org/10.1016/j.apt.2019.07.033

Filipović S, Obradović N, Marković S, Mitrić M, Balać I, Đorđević A, Pavlović VB. The effect of ball milling on properties of sintered manganese-doped alumina. in Advanced Powder Technology. 2019;30(11):2533-2540.
doi:10.1016/j.apt.2019.07.033 .

Filipović, Suzana, Obradović, Nina, Marković, Smilja, Mitrić, Miodrag, Balać, Igor, Đorđević, Antonije, Pavlović, Vladimir B., "The effect of ball milling on properties of sintered manganese-doped alumina" in Advanced Powder Technology, 30, no. 11 (2019):2533-2540,
https://doi.org/10.1016/j.apt.2019.07.033 . .