@conference{
author = "Jelić, Marko and Korneeva, Ekaterina and Kirilkin, Nikita and Vershinina, Tatiana and Orelovich, Oleg and Skuratov, Vladimir and Jovanović, Zoran and Jovanović, Sonja",
year = "2023",
abstract = "Monoclinic bismuth vanadate (BiVO4) is considered to be one of the most promising photoanode materials for photoelectrochemical (PEC) water splitting due to its suitable band gap and band structure, good stability and low-cost synthesis. However, BiVO4 has poor charge transfer properties due to the high rate of electron-hole recombination and understanding the effects contributing to it is important for further improvements. Herein, we report the effect of swift heavy ion irradiation (Xe, 150 MeV, 1010 – 5×1011 ions/cm2 ) on physicochemical properties of hydrothermally synthesized BiVO4 thin films. X-ray diffraction study (XRD) showed that irradiated material preserved initial monoclinic scheelite crystal phase and preferential growth along [010] direction. As the fluence increased, a shift of the diffraction maxima towards lower 2θ values was observed indicating increased interplanar distances. Also, for the 5×1011 ions/cm2 irradiated sample, high degree of amorphization was noticed. Scanning electron microscopy (SEM) of all samples showed prismatic grains with an average size of 600 nm. In irradiated samples formation of ion tracks, ~10 nm in diameter, was observed. X-ray photoelectron spectroscopy (XPS) analysis of Bi 4f, V 2p and O 1s states showed that, after irradiation, increased amounts of V4+ and oxygen in the form of hydroxide occurred, especially at higher fluences. By using UV-Vis Diffuse Reflectance spectroscopy we showed that band gap decreased with the increase of fluence. Photocurrent densities obtained from linear sweep voltammetry indicated that irradiation with fluences higher than 1010 ions/cm2 have a notable negative effect on PEC oxygen evolution reaction. However, 1-hour-long chronoamperometry measurements of 1010 ions/cm2 irradiated sample revealed an increase of photocurrent densities. In order to get a better insight into preceding phenomena, we performed XRD, SEM and XPS analysis after PEC process.",
publisher = "Belgrade : Materials Research Society of Serbia",
journal = "YUCOMAT 2023 : 24th Annual Conference YUCOMAT 2023 : programme and the book of abstracts; September 4-8, 2023; Herceg Novi, Montenegro",
title = "The effect of swift heavy ion irradiation on physicochemical properties of monoclinic bismuth vanadate",
pages = "95",
url = "https://hdl.handle.net/21.15107/rcub_vinar_11654"
}