TY  - JOUR
AU  - Pantović Pavlović, Marijana R.
AU  - Pavlović, Miroslav M.
AU  - Eraković, Sanja
AU  - Barudžija, Tanja
AU  - Stevanović, Jasmina S.
AU  - Ignjatović, Nenad L.
AU  - Panić, Vladimir V.
PY  - 2019
UR  - https://www.shd-pub.org.rs/index.php/JSCS/article/view/8524
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/8671
AB  - The optimization of the anodization process of Ti substrate for in situ synthesis of hydroxyapatite/titanium oxide composite coatings on titanium substrate was accomplished. The anodization was performed under 30, 60 and 90 V cell voltage, and the morphology of treated surface, as well as linear and surface roughness, were analysed by field emission-scanning electron micro­scopy, atomic force microscopy and roughness tester. It was shown by linear and surface roughness analyses that titanium anodized under 60 V has the high­est roughness, whereas at 90 V the flattening of the surface occurs. As the highest surface roughness results emerged at 60 V, the novel process of com­po­site anHAp/TiO2 coating synthesis, which comprises simultaneous processes of TiO2 formation and HAp deposition, as well as HAp impregnation within TiO2 surface layer, was performed at this voltage. Ti substrate surface was completely covered by composite coating, with no visible cracks. The adhesion quantified according to ASTM D3359-02 standard is considerably improved with respect to the coatings obtained by cathaphoretic processes, with no need of subsequent sintering.
T2  - Journal of the Serbian Chemical Society
T1  - Relationship between the properties of an interlayer formed by in situ Ti anodization and anaphoretically deposited hydroxyapatite
VL  - 84
IS  - 11
SP  - 1305
EP  - 1318
DO  - 10.2298/JSC190730105P
ER  - 

@article{
author = "Pantović Pavlović, Marijana R. and Pavlović, Miroslav M. and Eraković, Sanja and Barudžija, Tanja and Stevanović, Jasmina S. and Ignjatović, Nenad L. and Panić, Vladimir V.",
year = "2019",
abstract = "The optimization of the anodization process of Ti substrate for in situ synthesis of hydroxyapatite/titanium oxide composite coatings on titanium substrate was accomplished. The anodization was performed under 30, 60 and 90 V cell voltage, and the morphology of treated surface, as well as linear and surface roughness, were analysed by field emission-scanning electron micro­scopy, atomic force microscopy and roughness tester. It was shown by linear and surface roughness analyses that titanium anodized under 60 V has the high­est roughness, whereas at 90 V the flattening of the surface occurs. As the highest surface roughness results emerged at 60 V, the novel process of com­po­site anHAp/TiO2 coating synthesis, which comprises simultaneous processes of TiO2 formation and HAp deposition, as well as HAp impregnation within TiO2 surface layer, was performed at this voltage. Ti substrate surface was completely covered by composite coating, with no visible cracks. The adhesion quantified according to ASTM D3359-02 standard is considerably improved with respect to the coatings obtained by cathaphoretic processes, with no need of subsequent sintering.",
journal = "Journal of the Serbian Chemical Society",
title = "Relationship between the properties of an interlayer formed by in situ Ti anodization and anaphoretically deposited hydroxyapatite",
volume = "84",
number = "11",
pages = "1305-1318",
doi = "10.2298/JSC190730105P"
}

Pantović Pavlović, M. R., Pavlović, M. M., Eraković, S., Barudžija, T., Stevanović, J. S., Ignjatović, N. L.,& Panić, V. V.. (2019). Relationship between the properties of an interlayer formed by in situ Ti anodization and anaphoretically deposited hydroxyapatite. in Journal of the Serbian Chemical Society, 84(11), 1305-1318.
https://doi.org/10.2298/JSC190730105P

Pantović Pavlović MR, Pavlović MM, Eraković S, Barudžija T, Stevanović JS, Ignjatović NL, Panić VV. Relationship between the properties of an interlayer formed by in situ Ti anodization and anaphoretically deposited hydroxyapatite. in Journal of the Serbian Chemical Society. 2019;84(11):1305-1318.
doi:10.2298/JSC190730105P .

Pantović Pavlović, Marijana R., Pavlović, Miroslav M., Eraković, Sanja, Barudžija, Tanja, Stevanović, Jasmina S., Ignjatović, Nenad L., Panić, Vladimir V., "Relationship between the properties of an interlayer formed by in situ Ti anodization and anaphoretically deposited hydroxyapatite" in Journal of the Serbian Chemical Society, 84, no. 11 (2019):1305-1318,
https://doi.org/10.2298/JSC190730105P . .

TY  - JOUR
AU  - Eraković, Sanja
AU  - Pavlović, Miroslav M.
AU  - Stopić, Srećko
AU  - Stevanović, Jasmina
AU  - Mitrić, Miodrag
AU  - Friedrich, Bernd
AU  - Panić, Vladimir
PY  - 2019
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/8470
AB  - Considerable promotion of RuO2 hosted by perovskite-like structure of rare earth–CoO3 composite and vice versa supercapacitive performances is reported. Spherical, sub-μm-sized, regular spheres of La0.6Sr0.4CoO3 (LSCO), were synthesized by ultrasonic spray pyrolysis. The sphere surface was subsequently hydrothermally doped by RuO2. LSCO and LSCO/RuO2 composites were investigated for their supercapacitive performances in alkaline solution. Microstructure and surface morphology were studied by SEM and XRD. It was found that amorphous Ru species decorate LSCO surface, and possibly incorporate partially into B-site of the LSCO lattice. Electrochemical characterization by cyclic voltammetry (CV), galvanostatic charge-discharge (G-C/DC) and electrochemical impedance spectroscopy (EIS) clearly revealed that capacitive performances of LSCO are considerably improved by addition of 20 mass. % of RuO2. The registered capacitance for LSCO/RuO2 reaches the values of pure RuO2, which reveals the promoting influence of LSCO on RuO2 pseudocapacitance. The EIS analysis showed that RuO2 catalyzes the redox transition of Co species, with simultaneous proportional increase in pseudocapacitive RuO2 abilities while being hosted by LSCO. This intrinsic interactive promotion introduces LSCO/RuO2 composite as unique supercapacitive material. G-C/DC curves showed that LSCO/RuO2 is of modest cyclability with respect to pure LSCO and RuO2, although the capacitance losses with cycling are acceptably low. © 2019 Elsevier Ltd
T2  - Electrochimica Acta
T1  - Interactive promotion of supercapacitance of rare earth/CoO3-based spray pyrolytic perovskite microspheres hosting the hydrothermal ruthenium oxide
VL  - 321
SP  - 134721
DO  - 10.1016/j.electacta.2019.134721
ER  - 

@article{
author = "Eraković, Sanja and Pavlović, Miroslav M. and Stopić, Srećko and Stevanović, Jasmina and Mitrić, Miodrag and Friedrich, Bernd and Panić, Vladimir",
year = "2019",
abstract = "Considerable promotion of RuO2 hosted by perovskite-like structure of rare earth–CoO3 composite and vice versa supercapacitive performances is reported. Spherical, sub-μm-sized, regular spheres of La0.6Sr0.4CoO3 (LSCO), were synthesized by ultrasonic spray pyrolysis. The sphere surface was subsequently hydrothermally doped by RuO2. LSCO and LSCO/RuO2 composites were investigated for their supercapacitive performances in alkaline solution. Microstructure and surface morphology were studied by SEM and XRD. It was found that amorphous Ru species decorate LSCO surface, and possibly incorporate partially into B-site of the LSCO lattice. Electrochemical characterization by cyclic voltammetry (CV), galvanostatic charge-discharge (G-C/DC) and electrochemical impedance spectroscopy (EIS) clearly revealed that capacitive performances of LSCO are considerably improved by addition of 20 mass. % of RuO2. The registered capacitance for LSCO/RuO2 reaches the values of pure RuO2, which reveals the promoting influence of LSCO on RuO2 pseudocapacitance. The EIS analysis showed that RuO2 catalyzes the redox transition of Co species, with simultaneous proportional increase in pseudocapacitive RuO2 abilities while being hosted by LSCO. This intrinsic interactive promotion introduces LSCO/RuO2 composite as unique supercapacitive material. G-C/DC curves showed that LSCO/RuO2 is of modest cyclability with respect to pure LSCO and RuO2, although the capacitance losses with cycling are acceptably low. © 2019 Elsevier Ltd",
journal = "Electrochimica Acta",
title = "Interactive promotion of supercapacitance of rare earth/CoO3-based spray pyrolytic perovskite microspheres hosting the hydrothermal ruthenium oxide",
volume = "321",
pages = "134721",
doi = "10.1016/j.electacta.2019.134721"
}

Eraković, S., Pavlović, M. M., Stopić, S., Stevanović, J., Mitrić, M., Friedrich, B.,& Panić, V.. (2019). Interactive promotion of supercapacitance of rare earth/CoO3-based spray pyrolytic perovskite microspheres hosting the hydrothermal ruthenium oxide. in Electrochimica Acta, 321, 134721.
https://doi.org/10.1016/j.electacta.2019.134721

Eraković S, Pavlović MM, Stopić S, Stevanović J, Mitrić M, Friedrich B, Panić V. Interactive promotion of supercapacitance of rare earth/CoO3-based spray pyrolytic perovskite microspheres hosting the hydrothermal ruthenium oxide. in Electrochimica Acta. 2019;321:134721.
doi:10.1016/j.electacta.2019.134721 .

Eraković, Sanja, Pavlović, Miroslav M., Stopić, Srećko, Stevanović, Jasmina, Mitrić, Miodrag, Friedrich, Bernd, Panić, Vladimir, "Interactive promotion of supercapacitance of rare earth/CoO3-based spray pyrolytic perovskite microspheres hosting the hydrothermal ruthenium oxide" in Electrochimica Acta, 321 (2019):134721,
https://doi.org/10.1016/j.electacta.2019.134721 . .

TY  - JOUR
AU  - Avramović, Ljiljana
AU  - Ivanović, Evica R.
AU  - Maksimović, Vesna
AU  - Pavlović, Miroslav M.
AU  - Vuković, Marina
AU  - Stefanović, Jasmina S.
AU  - Nikolić, Nebojša D.
PY  - 2018
UR  - https://linkinghub.elsevier.com/retrieve/pii/S1003632618648356
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/7904
AB  - Silver dendritic nanonstructures obtained by the potentiostatic electrolysis from different electrolytes at different overpotentials were characterized by the scanning electron microscopy (SEM) technique and X-ray diffraction analysis of the produced particles. The needle-like and fern-like dendrites were formed from the nitrate electrolyte at overpotentials inside and outside plateaus of the limiting diffusion current density, respectively. The three-dimensional pine-like dendrites constructed from approximately spherical grains were formed from the ammonium electrolyte at overpotentials both inside and outside plateaus of the limiting diffusion current density. The morphology of silver dendrites was correlated with their crystal structure at the semi quantiative level. The change of crystal orientation from the strong (111) preferred orientation for the needle-like dendrites to almost randomly orientied spherical grains in the pine-like dendrites obtained at the overpotential outside the plateau of the limiting diffusion current density was observed. This trend in change of crystal orientation and morphology of Ag nanostructures was accompanied by considerable increase of the specific surface area (SSA) of the produced powders. The average crystallite sizes were in the range of 38–50 nm, proving nanostructural character of the formed Ag particles. © 2018 The Nonferrous Metals Society of China
T2  - Transactions of Nonferrous Metals Society of China
T1  - Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures
VL  - 28
IS  - 9
SP  - 1903
EP  - 1912
DO  - 10.1016/S1003-6326(18)64835-6
ER  - 

@article{
author = "Avramović, Ljiljana and Ivanović, Evica R. and Maksimović, Vesna and Pavlović, Miroslav M. and Vuković, Marina and Stefanović, Jasmina S. and Nikolić, Nebojša D.",
year = "2018",
abstract = "Silver dendritic nanonstructures obtained by the potentiostatic electrolysis from different electrolytes at different overpotentials were characterized by the scanning electron microscopy (SEM) technique and X-ray diffraction analysis of the produced particles. The needle-like and fern-like dendrites were formed from the nitrate electrolyte at overpotentials inside and outside plateaus of the limiting diffusion current density, respectively. The three-dimensional pine-like dendrites constructed from approximately spherical grains were formed from the ammonium electrolyte at overpotentials both inside and outside plateaus of the limiting diffusion current density. The morphology of silver dendrites was correlated with their crystal structure at the semi quantiative level. The change of crystal orientation from the strong (111) preferred orientation for the needle-like dendrites to almost randomly orientied spherical grains in the pine-like dendrites obtained at the overpotential outside the plateau of the limiting diffusion current density was observed. This trend in change of crystal orientation and morphology of Ag nanostructures was accompanied by considerable increase of the specific surface area (SSA) of the produced powders. The average crystallite sizes were in the range of 38–50 nm, proving nanostructural character of the formed Ag particles. © 2018 The Nonferrous Metals Society of China",
journal = "Transactions of Nonferrous Metals Society of China",
title = "Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures",
volume = "28",
number = "9",
pages = "1903-1912",
doi = "10.1016/S1003-6326(18)64835-6"
}

Avramović, L., Ivanović, E. R., Maksimović, V., Pavlović, M. M., Vuković, M., Stefanović, J. S.,& Nikolić, N. D.. (2018). Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures. in Transactions of Nonferrous Metals Society of China, 28(9), 1903-1912.
https://doi.org/10.1016/S1003-6326(18)64835-6

Avramović L, Ivanović ER, Maksimović V, Pavlović MM, Vuković M, Stefanović JS, Nikolić ND. Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures. in Transactions of Nonferrous Metals Society of China. 2018;28(9):1903-1912.
doi:10.1016/S1003-6326(18)64835-6 .

Avramović, Ljiljana, Ivanović, Evica R., Maksimović, Vesna, Pavlović, Miroslav M., Vuković, Marina, Stefanović, Jasmina S., Nikolić, Nebojša D., "Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures" in Transactions of Nonferrous Metals Society of China, 28, no. 9 (2018):1903-1912,
https://doi.org/10.1016/S1003-6326(18)64835-6 . .

TY  - JOUR
AU  - Avramović, Ljiljana
AU  - Pavlović, Miroslav M.
AU  - Maksimović, Vesna
AU  - Vuković, Marina
AU  - Stevanović, Jasmina S.
AU  - Bugarin, Mile
AU  - Nikolić, Nebojša D.
PY  - 2017
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/1612
AB  - Silver powders chemically synthesized by reduction with hydrazine and those produced by electrolysis from the basic ( nitrate) and complex ( ammonium) electrolytes were examined by X-ray diffraction (XRD) and scanning electron microscopic (SEM) analysis of the produced particles. Morphologies of the obtained particles were very different at the macro level. The needle-like dendrites, as well as the mixture of irregular and regular crystals, were formed from the nitrate electrolyte, while the highly-branched pine-like dendrites with clearly noticeable spherical grains were formed from the ammonium electrolyte. The agglomerates of spherical grains were formed by reduction with hydrazine. In the particles obtained from the nitrate electrolyte, Ag crystallites were strongly oriented in the (111) plane. Although morphologies of Ag particles were very different at the macro level, the similarity at the micro level was observed between chemically-synthesized particles and those obtained by electrolysis from the ammonium electrolyte. Both types of particles were constructed from the spherical grains. This similarity at the micro level was accompanied by the similar XRD patterns, which were very close to the Ag standard with a random orientation of Ag crystallites. For the first time, morphologies of powder particles were correlated with their crystal structure.
T2  - Metals
T1  - Comparative Morphological and Crystallographic Analysis of Electrochemically- and Chemically-Produced Silver Powder Particles
VL  - 7
IS  - 5
DO  - 10.3390/met7050160
ER  - 

@article{
author = "Avramović, Ljiljana and Pavlović, Miroslav M. and Maksimović, Vesna and Vuković, Marina and Stevanović, Jasmina S. and Bugarin, Mile and Nikolić, Nebojša D.",
year = "2017",
abstract = "Silver powders chemically synthesized by reduction with hydrazine and those produced by electrolysis from the basic ( nitrate) and complex ( ammonium) electrolytes were examined by X-ray diffraction (XRD) and scanning electron microscopic (SEM) analysis of the produced particles. Morphologies of the obtained particles were very different at the macro level. The needle-like dendrites, as well as the mixture of irregular and regular crystals, were formed from the nitrate electrolyte, while the highly-branched pine-like dendrites with clearly noticeable spherical grains were formed from the ammonium electrolyte. The agglomerates of spherical grains were formed by reduction with hydrazine. In the particles obtained from the nitrate electrolyte, Ag crystallites were strongly oriented in the (111) plane. Although morphologies of Ag particles were very different at the macro level, the similarity at the micro level was observed between chemically-synthesized particles and those obtained by electrolysis from the ammonium electrolyte. Both types of particles were constructed from the spherical grains. This similarity at the micro level was accompanied by the similar XRD patterns, which were very close to the Ag standard with a random orientation of Ag crystallites. For the first time, morphologies of powder particles were correlated with their crystal structure.",
journal = "Metals",
title = "Comparative Morphological and Crystallographic Analysis of Electrochemically- and Chemically-Produced Silver Powder Particles",
volume = "7",
number = "5",
doi = "10.3390/met7050160"
}

Avramović, L., Pavlović, M. M., Maksimović, V., Vuković, M., Stevanović, J. S., Bugarin, M.,& Nikolić, N. D.. (2017). Comparative Morphological and Crystallographic Analysis of Electrochemically- and Chemically-Produced Silver Powder Particles. in Metals, 7(5).
https://doi.org/10.3390/met7050160

Avramović L, Pavlović MM, Maksimović V, Vuković M, Stevanović JS, Bugarin M, Nikolić ND. Comparative Morphological and Crystallographic Analysis of Electrochemically- and Chemically-Produced Silver Powder Particles. in Metals. 2017;7(5).
doi:10.3390/met7050160 .

Avramović, Ljiljana, Pavlović, Miroslav M., Maksimović, Vesna, Vuković, Marina, Stevanović, Jasmina S., Bugarin, Mile, Nikolić, Nebojša D., "Comparative Morphological and Crystallographic Analysis of Electrochemically- and Chemically-Produced Silver Powder Particles" in Metals, 7, no. 5 (2017),
https://doi.org/10.3390/met7050160 . .