@article{
author = "Grujičić, Marija and Mravik, Željko and Bajuk-Bogdanović, Danica and Vengust, Damjan and Jovanović, Zoran M. and Stojković Simatović, Ivana and Jovanović, Sonja",
year = "2022",
abstract = "U ovom radu prikazana su elektrohemijska svojstva kompozita grafen-oksida i nanočestica kobalt-ferita, kao i kobalt-ferita dopiranog sa cinkom i galijumom. Grafen-oksid (GO) sintetisan je modifikovanom Hamerovom metodom. Magnetne nanočestice sintetisane su solvotermalnom metodom, nakon čega je izvršena izmena oleinske kiseline dihidrokofeinskom kiselinom sa ciljem dobijanja hidrofilnog materijala. Kompoziti grafen-oksida i magnetnih nanočestica sintetisani su hidrotermalnom metodom, prilikom čega je udeo magnetnih čestica bio 5 i 15 težinskih % u odnosu na grafen-oksid. Rezultati rendgeno-strukturne i FTIR analize potvrdili su potpunu oksidaciju grafenskih slojeva. SEM i TEM analize pokazale su depoziciju magnetnih nanočestica na sloju grafen-oksida, bez promene veličine ili oblika nanočestica. FTIR analiza hidrotemalno tretiranog grafen-oksida i kompozita pokazala je da dolazi do delimične redukcije epoksi grupa, kao i da se uspostavlja vodonična veza između komponenti kompozita. Ciklovoltamogrami pokazuju da su kompoziti stabilni pri brzinama polarizacije od 5 do 400 mV s-1, kao i da je njihov kapacitet pretežno pseudokapacitivne prirode. Pseudokapacitivnost potiče od oksidoredukcionih reakcija H+ jona iz elektrolita i površinskih funkcionalnih grupa grafen oksida. Na osnovu ciklovoltamograma izračunati su specifični kapaciteti svih kompozita, pri čemu je najveću vrednost pokazao kompozit CFO_GO_15% koja iznosi 36,86 F g-1 pri brzini polarizacije od 5 mV s-1., This paper presents the electrochemical properties of graphene-oxide composites and nanoparticles of cobalt-ferrite, as well as cobalt-ferrite doped with zinc and gallium. Graphene-oxide (GO) was synthesized by a modified Hummer's method. The magnetic nanoparticles were synthesized by the solvothermal method, after which the oleic acid was exchanged with dihydrocaffeic acid to obtain the hydrophilic material. Composites of graphene-oxide and magnetic nanoparticles were synthesized by the hydrothermal method, where the share of magnetic particles was 5 and 15 wt.% on graphene-oxide. The results of X-ray structural and FTIR analysis confirmed the complete oxidation of graphene layers. SEM and TEM analyzes showed deposition of magnetic nanoparticles on the graphene-oxide layer, without changing the size or shape of the nanoparticles. FTIR analysis of hydrothermally treated graphene oxide and composites showed that there is a partial reduction of epoxy groups, also a hydrogen bond is established between the components of the composite. Cyclic voltammograms show that the composites are stable at polarization rates of 5-400 mV s-1, and that their capacity is predominantly pseudocapacitive in nature. Pseudocapacitance originates from the oxidoreduction reactions of H+ ions from electrolytes and surface functional groups of graphene-oxide. Based on the cyclic voltammograms, the specific capacities of all composites were calculated and the highest value being shown by the CFO_GO_15% composite, which is 36.86 F g-1 at a polarization rate of 5 mV s-1.",
journal = "Tehnika",
title = "Elektrohemijska svojstva kompozita grafen-oksida i kobalt-ferita dopiranog cinkom i galijumom, Electrochemical properties of composites of graphene-oxide and cobalt-ferrite doped with zink and gallium",
volume = "77",
number = "2",
pages = "155-162",
doi = "10.5937/tehnika2202155G"
}