TY  - JOUR
AU  - Vujančević, Jelena
AU  - Andričević, Pavao
AU  - Bjelajac, Anđelika
AU  - Đokić, Veljko R.
AU  - Popović, Maja
AU  - Rakočević, Zlatko Lj.
AU  - Horvath, Endre
AU  - Kollar, Marton
AU  - Nafradi, Balint
AU  - Schiller, Andreas
AU  - Domanski, Konrad
AU  - Forro, Laszlo
AU  - Pavlović, Vera P.
AU  - Janaćković, Đorđe T.
PY  - 2019
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/8538
AB  - Highly ordered, anodically grown TiO 2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO 2 /CH 3 NH 3 PbI 3 single crystals. The N-TiO 2 /perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels of halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures. © 2019
T2  - Ceramics International
T1  - Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping
VL  - 45
IS  - 8
SP  - 10013
EP  - 10020
DO  - 10.1016/j.ceramint.2019.02.045
ER  - 

@article{
author = "Vujančević, Jelena and Andričević, Pavao and Bjelajac, Anđelika and Đokić, Veljko R. and Popović, Maja and Rakočević, Zlatko Lj. and Horvath, Endre and Kollar, Marton and Nafradi, Balint and Schiller, Andreas and Domanski, Konrad and Forro, Laszlo and Pavlović, Vera P. and Janaćković, Đorđe T.",
year = "2019",
abstract = "Highly ordered, anodically grown TiO 2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO 2 /CH 3 NH 3 PbI 3 single crystals. The N-TiO 2 /perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels of halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures. © 2019",
journal = "Ceramics International",
title = "Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping",
volume = "45",
number = "8",
pages = "10013-10020",
doi = "10.1016/j.ceramint.2019.02.045"
}

Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V. R., Popović, M., Rakočević, Z. Lj., Horvath, E., Kollar, M., Nafradi, B., Schiller, A., Domanski, K., Forro, L., Pavlović, V. P.,& Janaćković, Đ. T.. (2019). Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. in Ceramics International, 45(8), 10013-10020.
https://doi.org/10.1016/j.ceramint.2019.02.045

Vujančević J, Andričević P, Bjelajac A, Đokić VR, Popović M, Rakočević ZL, Horvath E, Kollar M, Nafradi B, Schiller A, Domanski K, Forro L, Pavlović VP, Janaćković ĐT. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. in Ceramics International. 2019;45(8):10013-10020.
doi:10.1016/j.ceramint.2019.02.045 .

Vujančević, Jelena, Andričević, Pavao, Bjelajac, Anđelika, Đokić, Veljko R., Popović, Maja, Rakočević, Zlatko Lj., Horvath, Endre, Kollar, Marton, Nafradi, Balint, Schiller, Andreas, Domanski, Konrad, Forro, Laszlo, Pavlović, Vera P., Janaćković, Đorđe T., "Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping" in Ceramics International, 45, no. 8 (2019):10013-10020,
https://doi.org/10.1016/j.ceramint.2019.02.045 . .

TY  - JOUR
AU  - Vujančević, Jelena
AU  - Andričević, Pavao
AU  - Bjelajac, Anđelika
AU  - Đokić, Veljko R.
AU  - Popović, Maja
AU  - Rakočević, Zlatko Lj.
AU  - Horvath, Endre
AU  - Kollar, Marton
AU  - Nafradi, Balint
AU  - Schiller, Andreas
AU  - Domanski, Konrad
AU  - Forro, Laszlo
AU  - Pavlović, Vera P.
AU  - Janaćković, Đorđe T.
PY  - 2019
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/8539
AB  - Highly ordered, anodically grown TiO 2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO 2 /CH 3 NH 3 PbI 3 single crystals. The N-TiO 2 /perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels of halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures. © 2019
T2  - Ceramics International
T1  - Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping
VL  - 45
IS  - 8
SP  - 10013
EP  - 10020
DO  - 10.1016/j.ceramint.2019.02.045
ER  - 

@article{
author = "Vujančević, Jelena and Andričević, Pavao and Bjelajac, Anđelika and Đokić, Veljko R. and Popović, Maja and Rakočević, Zlatko Lj. and Horvath, Endre and Kollar, Marton and Nafradi, Balint and Schiller, Andreas and Domanski, Konrad and Forro, Laszlo and Pavlović, Vera P. and Janaćković, Đorđe T.",
year = "2019",
abstract = "Highly ordered, anodically grown TiO 2 nanotubes on titanium supports were annealed in ammonia atmosphere in order to incorporate nitrogen doping (≤2 at.%) in the titanium oxide lattice. FESEM micrographs revealed nanotubes with an average outer diameter of 101.5 ± 1.5 nm and an average wall thickness of about 13 nm. Anatase crystals were formed inside the tubes after annealing in ammonia atmosphere for 30 min. With further annealing, rutile peaks appeared due to the thermal oxidation of the foil and rise as the duration of heat treatment was increased. The concentration and chemical nature of nitrogen in the nanotube arrays can be correlated to the optical response of dry-pressed heterojunctions of doped TiO 2 /CH 3 NH 3 PbI 3 single crystals. The N-TiO 2 /perovskite heterojunction with the highest amount of interstitial nitrogen exhibited an improved photocurrent, indicating the importance of the semiconductor doping-based heterojunction optimization strategies to deliver competitive levels of halide perovskite-based optoelectronic devices to be envisioned for urban infrastructures. © 2019",
journal = "Ceramics International",
title = "Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping",
volume = "45",
number = "8",
pages = "10013-10020",
doi = "10.1016/j.ceramint.2019.02.045"
}

Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V. R., Popović, M., Rakočević, Z. Lj., Horvath, E., Kollar, M., Nafradi, B., Schiller, A., Domanski, K., Forro, L., Pavlović, V. P.,& Janaćković, Đ. T.. (2019). Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. in Ceramics International, 45(8), 10013-10020.
https://doi.org/10.1016/j.ceramint.2019.02.045

Vujančević J, Andričević P, Bjelajac A, Đokić VR, Popović M, Rakočević ZL, Horvath E, Kollar M, Nafradi B, Schiller A, Domanski K, Forro L, Pavlović VP, Janaćković ĐT. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. in Ceramics International. 2019;45(8):10013-10020.
doi:10.1016/j.ceramint.2019.02.045 .

Vujančević, Jelena, Andričević, Pavao, Bjelajac, Anđelika, Đokić, Veljko R., Popović, Maja, Rakočević, Zlatko Lj., Horvath, Endre, Kollar, Marton, Nafradi, Balint, Schiller, Andreas, Domanski, Konrad, Forro, Laszlo, Pavlović, Vera P., Janaćković, Đorđe T., "Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping" in Ceramics International, 45, no. 8 (2019):10013-10020,
https://doi.org/10.1016/j.ceramint.2019.02.045 . .