TY  - JOUR
AU  - Peruško, Davor
AU  - Cizmovic, M.
AU  - Petrović, Suzana
AU  - Siketic, Z.
AU  - Mitrić, Miodrag
AU  - Pelicon, P.
AU  - Dražić, Goran
AU  - Kovač, Janez
AU  - Milinović, Velimir
AU  - Milosavljević, Momir
PY  - 2013
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/5457
AB  - Multilayered 5x(Al/Ti) structures, deposited on a Si substrate to a total thickness of 130 nm, were treated by unfocused Nd:YAG laser pulses (150 ps) with energies of 85 and 65 mJ. Irradiations were performed in air with 10, 50 and 100 successive laser pulses. Characterizations were done by using Rutherford backscattering spectrometry (RBS), elastic recoil detection analysis (ERDA), x-ray diffraction (XRD) and transmission electron microscopy (TEM). The results obtained show that laser irradiation, at either energy, induced almost full intermixing of deposited layers and formation of intermetallic compounds, but this was more pronounced for the applied laser pulses with a higher energy. The intermixed layer-silicon interface remains intact for all numbers of applied laser pulses and for both energies. The formation of an oxide layer on the sample surfaces was also observed, the thickness of which is greater for the higher laser beam energy.
T2  - Laser Physics
T1  - Laser irradiation of nano-metric Al/Ti multilayers
VL  - 23
IS  - 3
DO  - 10.1088/1054-660X/23/3/036005
ER  - 

@article{
author = "Peruško, Davor and Cizmovic, M. and Petrović, Suzana and Siketic, Z. and Mitrić, Miodrag and Pelicon, P. and Dražić, Goran and Kovač, Janez and Milinović, Velimir and Milosavljević, Momir",
year = "2013",
abstract = "Multilayered 5x(Al/Ti) structures, deposited on a Si substrate to a total thickness of 130 nm, were treated by unfocused Nd:YAG laser pulses (150 ps) with energies of 85 and 65 mJ. Irradiations were performed in air with 10, 50 and 100 successive laser pulses. Characterizations were done by using Rutherford backscattering spectrometry (RBS), elastic recoil detection analysis (ERDA), x-ray diffraction (XRD) and transmission electron microscopy (TEM). The results obtained show that laser irradiation, at either energy, induced almost full intermixing of deposited layers and formation of intermetallic compounds, but this was more pronounced for the applied laser pulses with a higher energy. The intermixed layer-silicon interface remains intact for all numbers of applied laser pulses and for both energies. The formation of an oxide layer on the sample surfaces was also observed, the thickness of which is greater for the higher laser beam energy.",
journal = "Laser Physics",
title = "Laser irradiation of nano-metric Al/Ti multilayers",
volume = "23",
number = "3",
doi = "10.1088/1054-660X/23/3/036005"
}

Peruško, D., Cizmovic, M., Petrović, S., Siketic, Z., Mitrić, M., Pelicon, P., Dražić, G., Kovač, J., Milinović, V.,& Milosavljević, M.. (2013). Laser irradiation of nano-metric Al/Ti multilayers. in Laser Physics, 23(3).
https://doi.org/10.1088/1054-660X/23/3/036005

Peruško D, Cizmovic M, Petrović S, Siketic Z, Mitrić M, Pelicon P, Dražić G, Kovač J, Milinović V, Milosavljević M. Laser irradiation of nano-metric Al/Ti multilayers. in Laser Physics. 2013;23(3).
doi:10.1088/1054-660X/23/3/036005 .

Peruško, Davor, Cizmovic, M., Petrović, Suzana, Siketic, Z., Mitrić, Miodrag, Pelicon, P., Dražić, Goran, Kovač, Janez, Milinović, Velimir, Milosavljević, Momir, "Laser irradiation of nano-metric Al/Ti multilayers" in Laser Physics, 23, no. 3 (2013),
https://doi.org/10.1088/1054-660X/23/3/036005 . .

TY  - JOUR
AU  - Petrović, Suzana
AU  - Radak, Bojan
AU  - Peruško, Davor
AU  - Pelicon, P.
AU  - Kovač, Janez
AU  - Mitrić, Miodrag
AU  - Gaković, Biljana M.
AU  - Trtica, Milan
PY  - 2013
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/5187
AB  - Laser-induced alloying effects on the composition and structure of different Ni/Ti multilayer structures were studied. Thin films composed of one, five, and ten (Ni/Ti) bilayers were deposited by DC ion sputtering on (1 0 0) Si wafers. Laser irradiations were performed by 150 ps pulses of a Nd:YAG laser operating at 1064 nm. The samples were characterized by Rutherford backscattering spectrometry (RBS), Auger electron spectroscopy (AES), X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). At a laser fluence of 0.9 J cm(-2), interaction between Ni and Ti layers was initiated, and NiTi alloy formed in 5- and 10-bilayered samples. Progressed alloying was achieved at a laser fluence of 1.2 J cm(-2). The alloy was formed mostly within the heat affected zone (HAZ) of the sample. Surface segregation of titanium was followed by formation of a 25 nm thin TiO2 film on the surface of the multilayered structures. In addition, parallel periodic surface structures on the surfaces of the 5- and 10-bilayered samples were clearly recorded. Their period in the case of the 5-bilayered system (0.77 mu m) agrees very well with the predictions of the common theory, whereas, in the case of the 10-bilayered system, two periods of such structures are observed (1.43 mu m and 0.4 mu m), and none of them coincides with the prediction. (C) 2012 Elsevier B. V. All rights reserved.
T2  - Applied Surface Science
T1  - Laser-induced surface alloying in nanosized Ni/Ti multilayer structures
VL  - 264
SP  - 273
EP  - 279
DO  - 10.1016/j.apsusc.2012.10.012
ER  - 

@article{
author = "Petrović, Suzana and Radak, Bojan and Peruško, Davor and Pelicon, P. and Kovač, Janez and Mitrić, Miodrag and Gaković, Biljana M. and Trtica, Milan",
year = "2013",
abstract = "Laser-induced alloying effects on the composition and structure of different Ni/Ti multilayer structures were studied. Thin films composed of one, five, and ten (Ni/Ti) bilayers were deposited by DC ion sputtering on (1 0 0) Si wafers. Laser irradiations were performed by 150 ps pulses of a Nd:YAG laser operating at 1064 nm. The samples were characterized by Rutherford backscattering spectrometry (RBS), Auger electron spectroscopy (AES), X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). At a laser fluence of 0.9 J cm(-2), interaction between Ni and Ti layers was initiated, and NiTi alloy formed in 5- and 10-bilayered samples. Progressed alloying was achieved at a laser fluence of 1.2 J cm(-2). The alloy was formed mostly within the heat affected zone (HAZ) of the sample. Surface segregation of titanium was followed by formation of a 25 nm thin TiO2 film on the surface of the multilayered structures. In addition, parallel periodic surface structures on the surfaces of the 5- and 10-bilayered samples were clearly recorded. Their period in the case of the 5-bilayered system (0.77 mu m) agrees very well with the predictions of the common theory, whereas, in the case of the 10-bilayered system, two periods of such structures are observed (1.43 mu m and 0.4 mu m), and none of them coincides with the prediction. (C) 2012 Elsevier B. V. All rights reserved.",
journal = "Applied Surface Science",
title = "Laser-induced surface alloying in nanosized Ni/Ti multilayer structures",
volume = "264",
pages = "273-279",
doi = "10.1016/j.apsusc.2012.10.012"
}

Petrović, S., Radak, B., Peruško, D., Pelicon, P., Kovač, J., Mitrić, M., Gaković, B. M.,& Trtica, M.. (2013). Laser-induced surface alloying in nanosized Ni/Ti multilayer structures. in Applied Surface Science, 264, 273-279.
https://doi.org/10.1016/j.apsusc.2012.10.012

Petrović S, Radak B, Peruško D, Pelicon P, Kovač J, Mitrić M, Gaković BM, Trtica M. Laser-induced surface alloying in nanosized Ni/Ti multilayer structures. in Applied Surface Science. 2013;264:273-279.
doi:10.1016/j.apsusc.2012.10.012 .

Petrović, Suzana, Radak, Bojan, Peruško, Davor, Pelicon, P., Kovač, Janez, Mitrić, Miodrag, Gaković, Biljana M., Trtica, Milan, "Laser-induced surface alloying in nanosized Ni/Ti multilayer structures" in Applied Surface Science, 264 (2013):273-279,
https://doi.org/10.1016/j.apsusc.2012.10.012 . .