TY  - JOUR
AU  - Amati, Matteo
AU  - Gregoratti, Luca
AU  - Sezen, Hikmet
AU  - Grce, Ana
AU  - Milosavljević, Momir
AU  - Homewood, Kevin P.
PY  - 2017
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/1578
AB  - This paper reports on compositional and structural modifications induced in coated AlN/TiN multilayers by argon ion irradiation. The initial structure consisting of totally 30 alternate AlN (8 nm thick) and TiN (9.3 nm thick) layers was deposited on Si (100) wafers, by reactive sputtering. Irradiation was done with 180 keV Ar+ to a high dose of 8 x 10(16) ions/cm(2), which introduces up to similar to 10 at.% of argon species, and generates a maximum displacement per atom of 92 for AlN and 127 for TiN, around the projected ion range (109 +/- 34 nm). Characterizations were performed by Rutherford backscattering spectrometry, spatially resolved x-ray photoelectron spectroscopy, and transmission electron microscopy. The obtained results reveal that this highly immiscible and thermally stable system suffered a severe modification upon the applied ion irradiation, although it was performed at room temperature. They illustrate a thorough inter-layer mixing, atomic redistribution, structural change and phase transformation within the affected depth. The original TiN layers appear to grow in thickness, consuming the adjacent AlN layers, while retaining the fcc crystalline structure. In the mostly affected region, the interaction proceeds until all of the original AlN layers are consumed. Compositional studies with photoemission spectroscopy show that due to the ion irradiation treatment the TiN and AlN layers are transformed into Ti0.75Al0.25N and Ti0.65Al0.35N ternary compounds characterized by a better homogenized chemical form compared to non-irradiated layers. The results can be interesting towards further development of radiation tolerant materials based on immiscible ceramic nanocomposites. (C) 2017 Elsevier B.V. All rights reserved.
T2  - Applied Surface Science
T1  - Compositional and structural studies of ion-beam modified AlN/TiN multilayers
VL  - 411
SP  - 431
EP  - 436
DO  - 10.1016/j.apsusc.2017.03.160
ER  - 

@article{
author = "Amati, Matteo and Gregoratti, Luca and Sezen, Hikmet and Grce, Ana and Milosavljević, Momir and Homewood, Kevin P.",
year = "2017",
abstract = "This paper reports on compositional and structural modifications induced in coated AlN/TiN multilayers by argon ion irradiation. The initial structure consisting of totally 30 alternate AlN (8 nm thick) and TiN (9.3 nm thick) layers was deposited on Si (100) wafers, by reactive sputtering. Irradiation was done with 180 keV Ar+ to a high dose of 8 x 10(16) ions/cm(2), which introduces up to similar to 10 at.% of argon species, and generates a maximum displacement per atom of 92 for AlN and 127 for TiN, around the projected ion range (109 +/- 34 nm). Characterizations were performed by Rutherford backscattering spectrometry, spatially resolved x-ray photoelectron spectroscopy, and transmission electron microscopy. The obtained results reveal that this highly immiscible and thermally stable system suffered a severe modification upon the applied ion irradiation, although it was performed at room temperature. They illustrate a thorough inter-layer mixing, atomic redistribution, structural change and phase transformation within the affected depth. The original TiN layers appear to grow in thickness, consuming the adjacent AlN layers, while retaining the fcc crystalline structure. In the mostly affected region, the interaction proceeds until all of the original AlN layers are consumed. Compositional studies with photoemission spectroscopy show that due to the ion irradiation treatment the TiN and AlN layers are transformed into Ti0.75Al0.25N and Ti0.65Al0.35N ternary compounds characterized by a better homogenized chemical form compared to non-irradiated layers. The results can be interesting towards further development of radiation tolerant materials based on immiscible ceramic nanocomposites. (C) 2017 Elsevier B.V. All rights reserved.",
journal = "Applied Surface Science",
title = "Compositional and structural studies of ion-beam modified AlN/TiN multilayers",
volume = "411",
pages = "431-436",
doi = "10.1016/j.apsusc.2017.03.160"
}

Amati, M., Gregoratti, L., Sezen, H., Grce, A., Milosavljević, M.,& Homewood, K. P.. (2017). Compositional and structural studies of ion-beam modified AlN/TiN multilayers. in Applied Surface Science, 411, 431-436.
https://doi.org/10.1016/j.apsusc.2017.03.160

Amati M, Gregoratti L, Sezen H, Grce A, Milosavljević M, Homewood KP. Compositional and structural studies of ion-beam modified AlN/TiN multilayers. in Applied Surface Science. 2017;411:431-436.
doi:10.1016/j.apsusc.2017.03.160 .

Amati, Matteo, Gregoratti, Luca, Sezen, Hikmet, Grce, Ana, Milosavljević, Momir, Homewood, Kevin P., "Compositional and structural studies of ion-beam modified AlN/TiN multilayers" in Applied Surface Science, 411 (2017):431-436,
https://doi.org/10.1016/j.apsusc.2017.03.160 . .