AB  - Nano-sized titanium monoxide (TiO) powder was prepared by mechanochemical synthesis. A mixture of commercial Ti and TiO2 (rutile) powders with the molar ratio of 1:1 was milled in a planetary ball mill for 5, 10, 20, 30 and 60 min under argon atmosphere. The final single-phase titanium monoxide sample was characterized by X-ray diffraction (XRD), magnetic measurements using a superconducting quantum interference device magnetometer (SQUID) and thermogravimetric analysis (TGA). The temperature dependency of the magnetic susceptibility is characterized by significant contribution of Pauli paramagnetism due to conduction electrons.
T2  - Hemijska industrija
T1  - Structural and magnetic properties of mechanochemically synthesized nanocrystalline titanium monoxide
VL  - 66
IS  - 2
SP  - 181
EP  - 186
DO  - 10.2298/HEMIND111027090B
ER  - 

@article{
author = "Barudžija, Tanja and Gusev, Alexey A. and Jugović, Dragana and Dramićanin, Miroslav and Zdujić, Miodrag and Jovalekić, Čedomir and Mitrić, Miodrag",
year = "2012",
abstract = "Nano-sized titanium monoxide (TiO) powder was prepared by mechanochemical synthesis. A mixture of commercial Ti and TiO2 (rutile) powders with the molar ratio of 1:1 was milled in a planetary ball mill for 5, 10, 20, 30 and 60 min under argon atmosphere. The final single-phase titanium monoxide sample was characterized by X-ray diffraction (XRD), magnetic measurements using a superconducting quantum interference device magnetometer (SQUID) and thermogravimetric analysis (TGA). The temperature dependency of the magnetic susceptibility is characterized by significant contribution of Pauli paramagnetism due to conduction electrons.",
journal = "Hemijska industrija",
title = "Structural and magnetic properties of mechanochemically synthesized nanocrystalline titanium monoxide",
volume = "66",
number = "2",
pages = "181-186",
doi = "10.2298/HEMIND111027090B"
}

Barudžija, T., Gusev, A. A., Jugović, D., Dramićanin, M., Zdujić, M., Jovalekić, Č.,& Mitrić, M.. (2012). Structural and magnetic properties of mechanochemically synthesized nanocrystalline titanium monoxide. in Hemijska industrija, 66(2), 181-186.
https://doi.org/10.2298/HEMIND111027090B

Barudžija T, Gusev AA, Jugović D, Dramićanin M, Zdujić M, Jovalekić Č, Mitrić M. Structural and magnetic properties of mechanochemically synthesized nanocrystalline titanium monoxide. in Hemijska industrija. 2012;66(2):181-186.
doi:10.2298/HEMIND111027090B .

Barudžija, Tanja, Gusev, Alexey A., Jugović, Dragana, Dramićanin, Miroslav, Zdujić, Miodrag, Jovalekić, Čedomir, Mitrić, Miodrag, "Structural and magnetic properties of mechanochemically synthesized nanocrystalline titanium monoxide" in Hemijska industrija, 66, no. 2 (2012):181-186,
https://doi.org/10.2298/HEMIND111027090B . .

TY  - JOUR
AU  - Barudžija, Tanja
AU  - Gusev, Alexey A.
AU  - Jugović, Dragana
AU  - Marinović-Cincović, Milena
AU  - Dramićanin, Miroslav
AU  - Zdujić, Miodrag
AU  - Jovalekić, Čedomir
AU  - Mitrić, Miodrag
PY  - 2012
UR  - https://vinar.vin.bg.ac.rs/handle/123456789/5133
AB  - Nanosized perovskite YTiO3 with mean crystallite size of 18 nm was synthesized for the first time by mechanochemical treatment. The mechanochemical solid state reaction between commercial Y2O3 powder and mechanochemically synthesized TiO powder in molar ratio 0.5:1 was performed over 3 h in a high-energy planetary ball mill in argon atmosphere. Heating in vacuum at 1150 degrees C for 12 h transforms nanosized YTiO3 to a well-crystallized single-phase perovskite YTiO3. Both samples were characterized by X-ray diffraction (XRD) and thermogravimetric (TGA/DTA) analyses, as well as superconducting quantum interference device magnetometer (SQUID) measurements.
T2  - Hemijska industrija
T1  - Structural and magnetic properties of mechanochemically synthesized nanosized yttrium titanate
VL  - 66
IS  - 3
SP  - 309
EP  - 315
DO  - 10.2298/HEMIND111103103B
ER  - 

@article{
author = "Barudžija, Tanja and Gusev, Alexey A. and Jugović, Dragana and Marinović-Cincović, Milena and Dramićanin, Miroslav and Zdujić, Miodrag and Jovalekić, Čedomir and Mitrić, Miodrag",
year = "2012",
abstract = "Nanosized perovskite YTiO3 with mean crystallite size of 18 nm was synthesized for the first time by mechanochemical treatment. The mechanochemical solid state reaction between commercial Y2O3 powder and mechanochemically synthesized TiO powder in molar ratio 0.5:1 was performed over 3 h in a high-energy planetary ball mill in argon atmosphere. Heating in vacuum at 1150 degrees C for 12 h transforms nanosized YTiO3 to a well-crystallized single-phase perovskite YTiO3. Both samples were characterized by X-ray diffraction (XRD) and thermogravimetric (TGA/DTA) analyses, as well as superconducting quantum interference device magnetometer (SQUID) measurements.",
journal = "Hemijska industrija",
title = "Structural and magnetic properties of mechanochemically synthesized nanosized yttrium titanate",
volume = "66",
number = "3",
pages = "309-315",
doi = "10.2298/HEMIND111103103B"
}

Barudžija, T., Gusev, A. A., Jugović, D., Marinović-Cincović, M., Dramićanin, M., Zdujić, M., Jovalekić, Č.,& Mitrić, M.. (2012). Structural and magnetic properties of mechanochemically synthesized nanosized yttrium titanate. in Hemijska industrija, 66(3), 309-315.
https://doi.org/10.2298/HEMIND111103103B

Barudžija T, Gusev AA, Jugović D, Marinović-Cincović M, Dramićanin M, Zdujić M, Jovalekić Č, Mitrić M. Structural and magnetic properties of mechanochemically synthesized nanosized yttrium titanate. in Hemijska industrija. 2012;66(3):309-315.
doi:10.2298/HEMIND111103103B .

Barudžija, Tanja, Gusev, Alexey A., Jugović, Dragana, Marinović-Cincović, Milena, Dramićanin, Miroslav, Zdujić, Miodrag, Jovalekić, Čedomir, Mitrić, Miodrag, "Structural and magnetic properties of mechanochemically synthesized nanosized yttrium titanate" in Hemijska industrija, 66, no. 3 (2012):309-315,
https://doi.org/10.2298/HEMIND111103103B . .