Antibacterial effects of new endodontic materials based on calcium silicates
Antibakterijski efekti novih endodontskih materijala na bazi kalcijum silikata
Аутори
Trišić, Dijana![](/themes/MirageVinar/images/orcid.png)
Ćetenović, Bojana
![](/themes/MirageVinar/images/orcid.png)
Zdravković, Nemanja M.
![](/themes/MirageVinar/images/orcid.png)
Marković, Tatjana
![](/themes/MirageVinar/images/orcid.png)
Dojčinović, Biljana P.
![](/themes/MirageVinar/images/orcid.png)
Jokanović, Vukoman R.
![](/themes/MirageVinar/images/orcid.png)
Marković, Dejan
![](/themes/MirageVinar/images/orcid.png)
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Background/Aim. The main task of endodontic treatment is to eliminate pathologically altered tissue, to disinfect root canal space and to obtain its three-dimensional hermetic obturation. The main purpose of this study was to evaluate antimicrobial activity of new endodontic nano-structured highly active calcium silicates based materials albo-mineral plyoxide carbonate aggregate (ALBO-MPCA) and calcium silicates (CS) in comparison to mineral trioxide aggregate (MTA+) and UltraCal XS (CH). Methods. The antimicrobial activity of materials was tested against Staphylococcus aureus (ATCC 25923) and Enterococcus faecalis (ATCC 14506) strains, and following clinical isolates: Rothia dentocariosa, Enterococcus faecalis, Staphylococcus aureus, Streptococcus anginosus and Streptococcus vestibularis using a double layer agar diffusion test. The pH measurements were performed using the pH meter. Total amount of released ions was determined by inductively coupled plasma optical emission spectrometr...y (ICP-OES). Results. All tested materials showed the best antibacterial potential after 1 h of incubation. After 3h and 24h of the incubation period, the antibacterial potential of all tested materials were similar. The Agar diffusion test showed that ALBO-MPCA, CS and MTA+ had similar inhibition zones (p > 0.05), except in the activity against Staphylococcus aureus where ALBO-MPCA showed better antimicrobial properties than MTA+ in 3h and 24h of the incubation period (p < 0.05). Following 24h of the incubation, the inhibition zones were the strongest with CH against Staphylococcus aureus (16.67 ± 2.34 mm) followed by ALBO-MPCA (14.67 ± 1.21 mm) and the weakest with CS against Enterococcus faecalis (6.50 ± 1.76 mm). CH showed the highest pH, followed by ALBO-MPCA, CS and MTA+. Conclusion. The expressed antibacterial effects indicate that materials based on nano-structured highly active calcium silicates represent effective therapeutic agents for root canal obturation in one-visit apexification treatment, therefore they are recommend for further examination and clinical trials as they are proposed for MTA substitution. © 2019, Inst. Sci. inf., Univ. Defence in Belgrade. All rights reserved.
Кључне речи:
dental pulp diseases / root canal preparation / calcium silicate / calcium hydroxide / anti-infective agentsИзвор:
Vojnosanitetski pregled, 2019, 76, 4, 365-372Финансирање / пројекти:
- Хемијско и структурно дизајнирање наноматеријала за примену у медицини и инжењерству ткива (RS-MESTD-Basic Research (BR or ON)-172026)
- Увођење и евалуација нове молекуларне методе за брзо откривање mecA гена стафилокока директно у брисевима узетим од људи, животиња и из њиховог окружења (RS-MESTD-Technological Development (TD or TR)-31079)
DOI: 10.2298/VSP161231130T
ISSN: 0042-8450
WoS: 000504432700002
Scopus: 2-s2.0-85069738071
Колекције
Институција/група
VinčaTY - JOUR AU - Trišić, Dijana AU - Ćetenović, Bojana AU - Zdravković, Nemanja M. AU - Marković, Tatjana AU - Dojčinović, Biljana P. AU - Jokanović, Vukoman R. AU - Marković, Dejan PY - 2019 UR - https://vinar.vin.bg.ac.rs/handle/123456789/8426 AB - Background/Aim. The main task of endodontic treatment is to eliminate pathologically altered tissue, to disinfect root canal space and to obtain its three-dimensional hermetic obturation. The main purpose of this study was to evaluate antimicrobial activity of new endodontic nano-structured highly active calcium silicates based materials albo-mineral plyoxide carbonate aggregate (ALBO-MPCA) and calcium silicates (CS) in comparison to mineral trioxide aggregate (MTA+) and UltraCal XS (CH). Methods. The antimicrobial activity of materials was tested against Staphylococcus aureus (ATCC 25923) and Enterococcus faecalis (ATCC 14506) strains, and following clinical isolates: Rothia dentocariosa, Enterococcus faecalis, Staphylococcus aureus, Streptococcus anginosus and Streptococcus vestibularis using a double layer agar diffusion test. The pH measurements were performed using the pH meter. Total amount of released ions was determined by inductively coupled plasma optical emission spectrometry (ICP-OES). Results. All tested materials showed the best antibacterial potential after 1 h of incubation. After 3h and 24h of the incubation period, the antibacterial potential of all tested materials were similar. The Agar diffusion test showed that ALBO-MPCA, CS and MTA+ had similar inhibition zones (p > 0.05), except in the activity against Staphylococcus aureus where ALBO-MPCA showed better antimicrobial properties than MTA+ in 3h and 24h of the incubation period (p < 0.05). Following 24h of the incubation, the inhibition zones were the strongest with CH against Staphylococcus aureus (16.67 ± 2.34 mm) followed by ALBO-MPCA (14.67 ± 1.21 mm) and the weakest with CS against Enterococcus faecalis (6.50 ± 1.76 mm). CH showed the highest pH, followed by ALBO-MPCA, CS and MTA+. Conclusion. The expressed antibacterial effects indicate that materials based on nano-structured highly active calcium silicates represent effective therapeutic agents for root canal obturation in one-visit apexification treatment, therefore they are recommend for further examination and clinical trials as they are proposed for MTA substitution. © 2019, Inst. Sci. inf., Univ. Defence in Belgrade. All rights reserved. T2 - Vojnosanitetski pregled T1 - Antibacterial effects of new endodontic materials based on calcium silicates VL - 76 IS - 4 SP - 365 EP - 372 DO - 10.2298/VSP161231130T ER -
@article{ author = "Trišić, Dijana and Ćetenović, Bojana and Zdravković, Nemanja M. and Marković, Tatjana and Dojčinović, Biljana P. and Jokanović, Vukoman R. and Marković, Dejan", year = "2019", abstract = "Background/Aim. The main task of endodontic treatment is to eliminate pathologically altered tissue, to disinfect root canal space and to obtain its three-dimensional hermetic obturation. The main purpose of this study was to evaluate antimicrobial activity of new endodontic nano-structured highly active calcium silicates based materials albo-mineral plyoxide carbonate aggregate (ALBO-MPCA) and calcium silicates (CS) in comparison to mineral trioxide aggregate (MTA+) and UltraCal XS (CH). Methods. The antimicrobial activity of materials was tested against Staphylococcus aureus (ATCC 25923) and Enterococcus faecalis (ATCC 14506) strains, and following clinical isolates: Rothia dentocariosa, Enterococcus faecalis, Staphylococcus aureus, Streptococcus anginosus and Streptococcus vestibularis using a double layer agar diffusion test. The pH measurements were performed using the pH meter. Total amount of released ions was determined by inductively coupled plasma optical emission spectrometry (ICP-OES). Results. All tested materials showed the best antibacterial potential after 1 h of incubation. After 3h and 24h of the incubation period, the antibacterial potential of all tested materials were similar. The Agar diffusion test showed that ALBO-MPCA, CS and MTA+ had similar inhibition zones (p > 0.05), except in the activity against Staphylococcus aureus where ALBO-MPCA showed better antimicrobial properties than MTA+ in 3h and 24h of the incubation period (p < 0.05). Following 24h of the incubation, the inhibition zones were the strongest with CH against Staphylococcus aureus (16.67 ± 2.34 mm) followed by ALBO-MPCA (14.67 ± 1.21 mm) and the weakest with CS against Enterococcus faecalis (6.50 ± 1.76 mm). CH showed the highest pH, followed by ALBO-MPCA, CS and MTA+. Conclusion. The expressed antibacterial effects indicate that materials based on nano-structured highly active calcium silicates represent effective therapeutic agents for root canal obturation in one-visit apexification treatment, therefore they are recommend for further examination and clinical trials as they are proposed for MTA substitution. © 2019, Inst. Sci. inf., Univ. Defence in Belgrade. All rights reserved.", journal = "Vojnosanitetski pregled", title = "Antibacterial effects of new endodontic materials based on calcium silicates", volume = "76", number = "4", pages = "365-372", doi = "10.2298/VSP161231130T" }
Trišić, D., Ćetenović, B., Zdravković, N. M., Marković, T., Dojčinović, B. P., Jokanović, V. R.,& Marković, D.. (2019). Antibacterial effects of new endodontic materials based on calcium silicates. in Vojnosanitetski pregled, 76(4), 365-372. https://doi.org/10.2298/VSP161231130T
Trišić D, Ćetenović B, Zdravković NM, Marković T, Dojčinović BP, Jokanović VR, Marković D. Antibacterial effects of new endodontic materials based on calcium silicates. in Vojnosanitetski pregled. 2019;76(4):365-372. doi:10.2298/VSP161231130T .
Trišić, Dijana, Ćetenović, Bojana, Zdravković, Nemanja M., Marković, Tatjana, Dojčinović, Biljana P., Jokanović, Vukoman R., Marković, Dejan, "Antibacterial effects of new endodontic materials based on calcium silicates" in Vojnosanitetski pregled, 76, no. 4 (2019):365-372, https://doi.org/10.2298/VSP161231130T . .