Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains
Autori
Kokunešoski, MajaBaščarević, Zvezdana D.
Rakočević, Zlatko Lj.
Šaponjić, Aleksandra
Šaponjić, Đorđe
Jordanov, Dragana
Babić, Biljana M.
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials were characterized by XRD, nitrogen adsorption desorption measurements, SEM, EDS and AFM analysis. It was found that small modifications of synthesis conditions influenced the morphological features of the synthesized SBA-15 samples. The SEM analysis had shown that the SBA-15 synthesized at lower temperature and longer time of reaction (80 degrees C, 48 h) provided elongated rod-shaped grains about 1 mu m long. The other sample synthesized at higher temperature and shorter time of reaction (100 degrees C, 24 h) had rounded grains and grains of regular spherical shape with diameters ranging from 0.5 to 2 mu m. The EDS analysis confirmed that the particles of both synthesized samples were of the SiO2 content. In addition, the AFM analysis had shown different surface m...orphologies of the materials synthesized under various conditions.
Ključne reči:
Mesoporous material / SBA-15 / Synthesis conditions / nanostructures / spherical grainsIzvor:
Science of Sintering, 2018, 50, 1, 111-121Finansiranje / projekti:
- Sinteza, procesiranje i karakterizacija nanostrukturnih materijala za primenu u oblasti energije, mehaničkog inženjerstva, zaštite životne stredine i biomedicine (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Funkcionalni, funkcionalizovani i usavršeni nano materijali (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45005)
- Vodonična energija - razvoj novih materijala: elektrolitičko dobijanje vodonika, vodonične gorivne ćelije, izotopski efekti (RS-MESTD-Basic Research (BR or ON)-172045)
DOI: 10.2298/SOS1801111K
ISSN: 0350-820X
WoS: 000429909100010
Scopus: 2-s2.0-85053925810
Kolekcije
Institucija/grupa
VinčaTY - JOUR AU - Kokunešoski, Maja AU - Baščarević, Zvezdana D. AU - Rakočević, Zlatko Lj. AU - Šaponjić, Aleksandra AU - Šaponjić, Đorđe AU - Jordanov, Dragana AU - Babić, Biljana M. PY - 2018 UR - https://vinar.vin.bg.ac.rs/handle/123456789/7650 AB - Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials were characterized by XRD, nitrogen adsorption desorption measurements, SEM, EDS and AFM analysis. It was found that small modifications of synthesis conditions influenced the morphological features of the synthesized SBA-15 samples. The SEM analysis had shown that the SBA-15 synthesized at lower temperature and longer time of reaction (80 degrees C, 48 h) provided elongated rod-shaped grains about 1 mu m long. The other sample synthesized at higher temperature and shorter time of reaction (100 degrees C, 24 h) had rounded grains and grains of regular spherical shape with diameters ranging from 0.5 to 2 mu m. The EDS analysis confirmed that the particles of both synthesized samples were of the SiO2 content. In addition, the AFM analysis had shown different surface morphologies of the materials synthesized under various conditions. T2 - Science of Sintering T1 - Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains VL - 50 IS - 1 SP - 111 EP - 121 DO - 10.2298/SOS1801111K ER -
@article{ author = "Kokunešoski, Maja and Baščarević, Zvezdana D. and Rakočević, Zlatko Lj. and Šaponjić, Aleksandra and Šaponjić, Đorđe and Jordanov, Dragana and Babić, Biljana M.", year = "2018", abstract = "Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials were characterized by XRD, nitrogen adsorption desorption measurements, SEM, EDS and AFM analysis. It was found that small modifications of synthesis conditions influenced the morphological features of the synthesized SBA-15 samples. The SEM analysis had shown that the SBA-15 synthesized at lower temperature and longer time of reaction (80 degrees C, 48 h) provided elongated rod-shaped grains about 1 mu m long. The other sample synthesized at higher temperature and shorter time of reaction (100 degrees C, 24 h) had rounded grains and grains of regular spherical shape with diameters ranging from 0.5 to 2 mu m. The EDS analysis confirmed that the particles of both synthesized samples were of the SiO2 content. In addition, the AFM analysis had shown different surface morphologies of the materials synthesized under various conditions.", journal = "Science of Sintering", title = "Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains", volume = "50", number = "1", pages = "111-121", doi = "10.2298/SOS1801111K" }
Kokunešoski, M., Baščarević, Z. D., Rakočević, Z. Lj., Šaponjić, A., Šaponjić, Đ., Jordanov, D.,& Babić, B. M.. (2018). Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains. in Science of Sintering, 50(1), 111-121. https://doi.org/10.2298/SOS1801111K
Kokunešoski M, Baščarević ZD, Rakočević ZL, Šaponjić A, Šaponjić Đ, Jordanov D, Babić BM. Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains. in Science of Sintering. 2018;50(1):111-121. doi:10.2298/SOS1801111K .
Kokunešoski, Maja, Baščarević, Zvezdana D., Rakočević, Zlatko Lj., Šaponjić, Aleksandra, Šaponjić, Đorđe, Jordanov, Dragana, Babić, Biljana M., "Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains" in Science of Sintering, 50, no. 1 (2018):111-121, https://doi.org/10.2298/SOS1801111K . .