Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja
Modification of structural, morphological and optical properties of anatase TiO2 nanoparticles doped with trivalent rare-earth ions.
Authors
Milićević, Bojana R.Contributors
Stojković-Simatović, IvanaDramićanin, Miroslav
Šljukić-Paunković, Biljana
Đorđević, Vesna R.
Minić-Popović, Dragica
Doctoral thesis
Metadata
Show full item recordAbstract
U ovoj doktorskoj disertaciji prikazana je temeljna studija modifikovanja strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja: prazeodijuma, neodijuma, samarijuma, europijuma, disprozijuma, terbijuma, holmijuma, erbijuma i tulijuma, pri koncentraciji od 1 at.%. Pomenuti materijali sintetisani su sol-gel tehnikom i žareni na temperaturi od 420 ºC. Strukturna svojstva nedopiranog anatas TiO2 kao i TiO2 dopiranоg jonima retkih zemalja ispitivana su rendgenskom difrakcionom analizom. Utvrđeno je da se sol-gel sintezom dobijaju čiste anatasne kristalne strukture sa veličinom kristalita od svega nekoliko nanometara. Uticaj jona retkih zemalja u anatasnoj kristalnoj strukturi titan-dioksida ogleda se u značajnom porastu specifične površine čestica. Takođe, sintetisani su nanoprahovi TiO2 koloidnom tehnikom u cilju korelisanja različitih metoda sinteza sa strukturnim, morfološkim i optičkim svojstvima...
The primary aim of this thesis is to explain the modification of structure, morphology and optical properties of anatase TiO2 nanoparticles doped with trivalent rare-earth ions: praseodymium, neodymium, samarium, europium, terbium, dysprosium, holmium, erbium, and thulium, with the concentration of 1 at.%. These materials were synthesized by the sol-gel technique and further annealed at 420 °C. Structural properties of anatase TiO2 and TiO2 doped with trivalent rare-earth ions are studied by X-ray diffraction analysis. It was confirmed that pure anatase TiO2 with the crystallite size of only a few nanometers was obtained by sol-gel synthesis. The incorporation of rare earth ions in the anatase TiO2 is reflected in the significant increase of the specific surface area of TiO2 nanopowders doped with rare-earth ions in comparison with undoped TiO2. Also, the TiO2 nanopowders were synthesized by a colloid technique to correlate the different methods of synthesis with structural, morphologi...cal and optical properties...
Keywords:
titan(IV)-oksid / Titan(IV)-oxide / joni retkih zemalja / luminescentni materijali / Li+-kodopiranje / fotokatalitički materijali / rare-earth ions / luminescent nanomaterials / lithium co-doping / photocatalytic nanomaterialsSource:
Универзитет у Београду, 2017Publisher:
- Универзитет у Београду, Факултет за физичку хемију
URI
http://eteze.bg.ac.rs/application/showtheses?thesesId=5384https://fedorabg.bg.ac.rs/fedora/get/o:16741/bdef:Content/download
http://vbs.rs/scripts/cobiss?command=DISPLAY&base=70036&RID=49501199
http://nardus.mpn.gov.rs/123456789/8915
https://vinar.vin.bg.ac.rs/handle/123456789/7327
Collections
Institution/Community
VinčaTY - THES AU - Milićević, Bojana R. PY - 2017 UR - http://eteze.bg.ac.rs/application/showtheses?thesesId=5384 UR - https://fedorabg.bg.ac.rs/fedora/get/o:16741/bdef:Content/download UR - http://vbs.rs/scripts/cobiss?command=DISPLAY&base=70036&RID=49501199 UR - http://nardus.mpn.gov.rs/123456789/8915 UR - https://vinar.vin.bg.ac.rs/handle/123456789/7327 AB - U ovoj doktorskoj disertaciji prikazana je temeljna studija modifikovanja strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja: prazeodijuma, neodijuma, samarijuma, europijuma, disprozijuma, terbijuma, holmijuma, erbijuma i tulijuma, pri koncentraciji od 1 at.%. Pomenuti materijali sintetisani su sol-gel tehnikom i žareni na temperaturi od 420 ºC. Strukturna svojstva nedopiranog anatas TiO2 kao i TiO2 dopiranоg jonima retkih zemalja ispitivana su rendgenskom difrakcionom analizom. Utvrđeno je da se sol-gel sintezom dobijaju čiste anatasne kristalne strukture sa veličinom kristalita od svega nekoliko nanometara. Uticaj jona retkih zemalja u anatasnoj kristalnoj strukturi titan-dioksida ogleda se u značajnom porastu specifične površine čestica. Takođe, sintetisani su nanoprahovi TiO2 koloidnom tehnikom u cilju korelisanja različitih metoda sinteza sa strukturnim, morfološkim i optičkim svojstvima... AB - The primary aim of this thesis is to explain the modification of structure, morphology and optical properties of anatase TiO2 nanoparticles doped with trivalent rare-earth ions: praseodymium, neodymium, samarium, europium, terbium, dysprosium, holmium, erbium, and thulium, with the concentration of 1 at.%. These materials were synthesized by the sol-gel technique and further annealed at 420 °C. Structural properties of anatase TiO2 and TiO2 doped with trivalent rare-earth ions are studied by X-ray diffraction analysis. It was confirmed that pure anatase TiO2 with the crystallite size of only a few nanometers was obtained by sol-gel synthesis. The incorporation of rare earth ions in the anatase TiO2 is reflected in the significant increase of the specific surface area of TiO2 nanopowders doped with rare-earth ions in comparison with undoped TiO2. Also, the TiO2 nanopowders were synthesized by a colloid technique to correlate the different methods of synthesis with structural, morphological and optical properties... PB - Универзитет у Београду, Факултет за физичку хемију T2 - Универзитет у Београду T1 - Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja UR - https://hdl.handle.net/21.15107/rcub_nardus_8915 ER -
@phdthesis{ author = "Milićević, Bojana R.", year = "2017", abstract = "U ovoj doktorskoj disertaciji prikazana je temeljna studija modifikovanja strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja: prazeodijuma, neodijuma, samarijuma, europijuma, disprozijuma, terbijuma, holmijuma, erbijuma i tulijuma, pri koncentraciji od 1 at.%. Pomenuti materijali sintetisani su sol-gel tehnikom i žareni na temperaturi od 420 ºC. Strukturna svojstva nedopiranog anatas TiO2 kao i TiO2 dopiranоg jonima retkih zemalja ispitivana su rendgenskom difrakcionom analizom. Utvrđeno je da se sol-gel sintezom dobijaju čiste anatasne kristalne strukture sa veličinom kristalita od svega nekoliko nanometara. Uticaj jona retkih zemalja u anatasnoj kristalnoj strukturi titan-dioksida ogleda se u značajnom porastu specifične površine čestica. Takođe, sintetisani su nanoprahovi TiO2 koloidnom tehnikom u cilju korelisanja različitih metoda sinteza sa strukturnim, morfološkim i optičkim svojstvima..., The primary aim of this thesis is to explain the modification of structure, morphology and optical properties of anatase TiO2 nanoparticles doped with trivalent rare-earth ions: praseodymium, neodymium, samarium, europium, terbium, dysprosium, holmium, erbium, and thulium, with the concentration of 1 at.%. These materials were synthesized by the sol-gel technique and further annealed at 420 °C. Structural properties of anatase TiO2 and TiO2 doped with trivalent rare-earth ions are studied by X-ray diffraction analysis. It was confirmed that pure anatase TiO2 with the crystallite size of only a few nanometers was obtained by sol-gel synthesis. The incorporation of rare earth ions in the anatase TiO2 is reflected in the significant increase of the specific surface area of TiO2 nanopowders doped with rare-earth ions in comparison with undoped TiO2. Also, the TiO2 nanopowders were synthesized by a colloid technique to correlate the different methods of synthesis with structural, morphological and optical properties...", publisher = "Универзитет у Београду, Факултет за физичку хемију", journal = "Универзитет у Београду", title = "Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja", url = "https://hdl.handle.net/21.15107/rcub_nardus_8915" }
Milićević, B. R.. (2017). Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja. in Универзитет у Београду Универзитет у Београду, Факултет за физичку хемију.. https://hdl.handle.net/21.15107/rcub_nardus_8915
Milićević BR. Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja. in Универзитет у Београду. 2017;. https://hdl.handle.net/21.15107/rcub_nardus_8915 .
Milićević, Bojana R., "Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja" in Универзитет у Београду (2017), https://hdl.handle.net/21.15107/rcub_nardus_8915 .