Sintering behaviour of nanosized HAP powder
Nema prikaza
Autori
Veljović, Đorđe N.Jokić, Bojan M.
Janković-Častvan, Ivona
Smičiklas, Ivana D.
Petrovic, R.
Janaćković, Đorđe T.
Konferencijski prilog
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.
Ključne reči:
hydroxyapatite / sintering / nanostructureIzvor:
Key Engineering Materials, 2007, 330-332, 259-+Finansiranje / projekti:
- Ministry of Science and Technology Republic of Serbia [142070B], EUREKA E [3033]
Napomena:
- 19th International Symposium on Ceramics in Medicine, Oct 10-13, 2006, Chengdu, Peoples R China
DOI: 10.4028/www.scientific.net/KEM.330-332.259
ISSN: 1013-9826
WoS: 000245026800064
[ Google Scholar ]Kolekcije
Institucija/grupa
VinčaTY - CONF AU - Veljović, Đorđe N. AU - Jokić, Bojan M. AU - Janković-Častvan, Ivona AU - Smičiklas, Ivana D. AU - Petrovic, R. AU - Janaćković, Đorđe T. PY - 2007 UR - https://vinar.vin.bg.ac.rs/handle/123456789/6645 AB - The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained. C3 - Key Engineering Materials T1 - Sintering behaviour of nanosized HAP powder VL - 330-332 SP - 259 EP - + DO - 10.4028/www.scientific.net/KEM.330-332.259 ER -
@conference{ author = "Veljović, Đorđe N. and Jokić, Bojan M. and Janković-Častvan, Ivona and Smičiklas, Ivana D. and Petrovic, R. and Janaćković, Đorđe T.", year = "2007", abstract = "The influences of temperature and time on sintering behaviour of nanosized HAP powder were investigate in this paper. The calcium hydroxyapatite powder, with the average crystallite size of 34 +/- 1 nm, was uniaxially pressed at a pressure of 500 MPa. Obtained green compacts were sintered at temperature ranging from 1000 degrees C to 1200 degrees C in air atmosphere at various times. According to the results of scanning electron microscopy, X-ray and FTIR analyses, it is shown that HAP compacts with dense microstructure and average grain size below 250 nm is obtained.", journal = "Key Engineering Materials", title = "Sintering behaviour of nanosized HAP powder", volume = "330-332", pages = "259-+", doi = "10.4028/www.scientific.net/KEM.330-332.259" }
Veljović, Đ. N., Jokić, B. M., Janković-Častvan, I., Smičiklas, I. D., Petrovic, R.,& Janaćković, Đ. T.. (2007). Sintering behaviour of nanosized HAP powder. in Key Engineering Materials, 330-332, 259-+. https://doi.org/10.4028/www.scientific.net/KEM.330-332.259
Veljović ĐN, Jokić BM, Janković-Častvan I, Smičiklas ID, Petrovic R, Janaćković ĐT. Sintering behaviour of nanosized HAP powder. in Key Engineering Materials. 2007;330-332:259-+. doi:10.4028/www.scientific.net/KEM.330-332.259 .
Veljović, Đorđe N., Jokić, Bojan M., Janković-Častvan, Ivona, Smičiklas, Ivana D., Petrovic, R., Janaćković, Đorđe T., "Sintering behaviour of nanosized HAP powder" in Key Engineering Materials, 330-332 (2007):259-+, https://doi.org/10.4028/www.scientific.net/KEM.330-332.259 . .