Moisture and gamma-ray irradiation effects on the mechanical properties of carbon fibre-reinforced plastics
Чланак у часопису
Метаподаци
Приказ свих података о документуАпстракт
The effects of gamma-irradiation and moisture absorption on the mechanical properties of carbon fibres-epoxy resin composites were studied. The properties dominated by the matrix and fibre-matrix interface (interlaminar and in-plane shear strength) were measured at room temperature using standard tests. These tests were carried out before and after exposures to gamma irradiation and before and after immersion in water at 80 degrees C during 21 days. The dosage of gamma irradiation was up to 11.7 MGy. The micrographs of surfaces fractured in performed tests were observed on a scanning electron microscope. They were analyzed with consulting the stated effects on mechanical properties and the measured values of the glass transition temperature of tested coupons before and after irradiation and immersion in water. The obtained results show that moisture and irradiation, if they act one after the other, have a significant influence on the degradation of matrix-dominated mechanical propertie...s of the tested carbon-epoxy composite.
Кључне речи:
Carbon fibre composite / epoxy resin / fractographic observation / interlaminar and in-plane shear strengths / moisture and irradiation effectsИзвор:
Journal of Microscopy, Oxford, 2008, 232, 3, 611-617Финансирање / пројекти:
- Наноструктурни неоксидни керамички и карбонски материјали и њихови композити (RS-MESTD-MPN2006-2010-142016)
DOI: 10.1111/j.1365-2818.2008.02126.x
ISSN: 0022-2720
PubMed: 19094048
WoS: 000261253200034
Scopus: 2-s2.0-57449106686
Колекције
Институција/група
VinčaTY - JOUR AU - Sekulić, Danijela R. AU - Božić, Dušan AU - Babić, Biljana M. AU - Stašić, Jelena AU - Stevanović, M. PY - 2008 UR - https://vinar.vin.bg.ac.rs/handle/123456789/3579 AB - The effects of gamma-irradiation and moisture absorption on the mechanical properties of carbon fibres-epoxy resin composites were studied. The properties dominated by the matrix and fibre-matrix interface (interlaminar and in-plane shear strength) were measured at room temperature using standard tests. These tests were carried out before and after exposures to gamma irradiation and before and after immersion in water at 80 degrees C during 21 days. The dosage of gamma irradiation was up to 11.7 MGy. The micrographs of surfaces fractured in performed tests were observed on a scanning electron microscope. They were analyzed with consulting the stated effects on mechanical properties and the measured values of the glass transition temperature of tested coupons before and after irradiation and immersion in water. The obtained results show that moisture and irradiation, if they act one after the other, have a significant influence on the degradation of matrix-dominated mechanical properties of the tested carbon-epoxy composite. T2 - Journal of Microscopy, Oxford T1 - Moisture and gamma-ray irradiation effects on the mechanical properties of carbon fibre-reinforced plastics VL - 232 IS - 3 SP - 611 EP - 617 DO - 10.1111/j.1365-2818.2008.02126.x ER -
@article{ author = "Sekulić, Danijela R. and Božić, Dušan and Babić, Biljana M. and Stašić, Jelena and Stevanović, M.", year = "2008", abstract = "The effects of gamma-irradiation and moisture absorption on the mechanical properties of carbon fibres-epoxy resin composites were studied. The properties dominated by the matrix and fibre-matrix interface (interlaminar and in-plane shear strength) were measured at room temperature using standard tests. These tests were carried out before and after exposures to gamma irradiation and before and after immersion in water at 80 degrees C during 21 days. The dosage of gamma irradiation was up to 11.7 MGy. The micrographs of surfaces fractured in performed tests were observed on a scanning electron microscope. They were analyzed with consulting the stated effects on mechanical properties and the measured values of the glass transition temperature of tested coupons before and after irradiation and immersion in water. The obtained results show that moisture and irradiation, if they act one after the other, have a significant influence on the degradation of matrix-dominated mechanical properties of the tested carbon-epoxy composite.", journal = "Journal of Microscopy, Oxford", title = "Moisture and gamma-ray irradiation effects on the mechanical properties of carbon fibre-reinforced plastics", volume = "232", number = "3", pages = "611-617", doi = "10.1111/j.1365-2818.2008.02126.x" }
Sekulić, D. R., Božić, D., Babić, B. M., Stašić, J.,& Stevanović, M.. (2008). Moisture and gamma-ray irradiation effects on the mechanical properties of carbon fibre-reinforced plastics. in Journal of Microscopy, Oxford, 232(3), 611-617. https://doi.org/10.1111/j.1365-2818.2008.02126.x
Sekulić DR, Božić D, Babić BM, Stašić J, Stevanović M. Moisture and gamma-ray irradiation effects on the mechanical properties of carbon fibre-reinforced plastics. in Journal of Microscopy, Oxford. 2008;232(3):611-617. doi:10.1111/j.1365-2818.2008.02126.x .
Sekulić, Danijela R., Božić, Dušan, Babić, Biljana M., Stašić, Jelena, Stevanović, M., "Moisture and gamma-ray irradiation effects on the mechanical properties of carbon fibre-reinforced plastics" in Journal of Microscopy, Oxford, 232, no. 3 (2008):611-617, https://doi.org/10.1111/j.1365-2818.2008.02126.x . .