Iron (III) Oxide Fabrication From Natural Clay With Reference to Phase Transformation gamma- - GT alpha- Fe2O3
Autori
Šaponjić, AleksandraŠaponjić, Đorđe
Nikolić, Violeta N.
Milošević, Maja
Marinović-Cincović, Milena
Gyoshev, Stanislav
Vuković, Marina
Kokunešoski, Maja
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Amorphous iron (III) oxide was obtained from clay, using ammonium hydroxide as a precipitating agent. Influence of freeze drying under vacuum, as a drying method, on particle size, chemical composition, and crystallinity of obtained iron (III) oxide powder was investigated. After freeze drying, precipitate was annealed in air at 500 C-o and 900 oC. X-ray diffraction, particle size analysis, scanning electron microscopy, energy dispersive spectrometry, Fourier transform infrared spectroscopy, thermogravimetric and differential thermal analysis were used to characterize obtained iron (III) oxide powder. All of three powders obtained by freeze drying and annealing, have low crystallinity and particles with irregular layered shape. Narrow particle size distribution was given by an average diameter value of around 50 mu m for all observed powders. Iron-bearing materials like a-Fe2O3 and gamma-Fe2O3 are obtained. Differential thermal analysis curve of obtained samples showed endothermic reac...tion at 620 oC which could be ascribed to phase transition from cubic form gamma- - GT alpha- Fe2O3. Thermal transformations of iron (III) oxide, obtained from clay as a natural source, is suitable to explore in the framework of materials chemistry, and opens the possibility to synthesize materials based on Fe2O3 with specific magnetic behavior.
Ključne reči:
Clay / Iron (III) oxide / Precipitation / Freeze drying / TG-DTAIzvor:
Science of Sintering, 2017, 49, 2, 197-205Finansiranje / projekti:
- Sinteza, procesiranje i karakterizacija nanostrukturnih materijala za primenu u oblasti energije, mehaničkog inženjerstva, zaštite životne stredine i biomedicine (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Vodonična energija - razvoj novih materijala: elektrolitičko dobijanje vodonika, vodonične gorivne ćelije, izotopski efekti (RS-MESTD-Basic Research (BR or ON)-172045)
- Magnetni i radionuklidima obeleženi nanostrukturni materijali za primene u medicini (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45015)
DOI: 10.2298/SOS1702197S
ISSN: 0350-820X
WoS: 000405578500010
Scopus: 2-s2.0-85026401622
Kolekcije
Institucija/grupa
VinčaTY - JOUR AU - Šaponjić, Aleksandra AU - Šaponjić, Đorđe AU - Nikolić, Violeta N. AU - Milošević, Maja AU - Marinović-Cincović, Milena AU - Gyoshev, Stanislav AU - Vuković, Marina AU - Kokunešoski, Maja PY - 2017 UR - https://vinar.vin.bg.ac.rs/handle/123456789/1644 AB - Amorphous iron (III) oxide was obtained from clay, using ammonium hydroxide as a precipitating agent. Influence of freeze drying under vacuum, as a drying method, on particle size, chemical composition, and crystallinity of obtained iron (III) oxide powder was investigated. After freeze drying, precipitate was annealed in air at 500 C-o and 900 oC. X-ray diffraction, particle size analysis, scanning electron microscopy, energy dispersive spectrometry, Fourier transform infrared spectroscopy, thermogravimetric and differential thermal analysis were used to characterize obtained iron (III) oxide powder. All of three powders obtained by freeze drying and annealing, have low crystallinity and particles with irregular layered shape. Narrow particle size distribution was given by an average diameter value of around 50 mu m for all observed powders. Iron-bearing materials like a-Fe2O3 and gamma-Fe2O3 are obtained. Differential thermal analysis curve of obtained samples showed endothermic reaction at 620 oC which could be ascribed to phase transition from cubic form gamma- - GT alpha- Fe2O3. Thermal transformations of iron (III) oxide, obtained from clay as a natural source, is suitable to explore in the framework of materials chemistry, and opens the possibility to synthesize materials based on Fe2O3 with specific magnetic behavior. T2 - Science of Sintering T1 - Iron (III) Oxide Fabrication From Natural Clay With Reference to Phase Transformation gamma- - GT alpha- Fe2O3 VL - 49 IS - 2 SP - 197 EP - 205 DO - 10.2298/SOS1702197S ER -
@article{ author = "Šaponjić, Aleksandra and Šaponjić, Đorđe and Nikolić, Violeta N. and Milošević, Maja and Marinović-Cincović, Milena and Gyoshev, Stanislav and Vuković, Marina and Kokunešoski, Maja", year = "2017", abstract = "Amorphous iron (III) oxide was obtained from clay, using ammonium hydroxide as a precipitating agent. Influence of freeze drying under vacuum, as a drying method, on particle size, chemical composition, and crystallinity of obtained iron (III) oxide powder was investigated. After freeze drying, precipitate was annealed in air at 500 C-o and 900 oC. X-ray diffraction, particle size analysis, scanning electron microscopy, energy dispersive spectrometry, Fourier transform infrared spectroscopy, thermogravimetric and differential thermal analysis were used to characterize obtained iron (III) oxide powder. All of three powders obtained by freeze drying and annealing, have low crystallinity and particles with irregular layered shape. Narrow particle size distribution was given by an average diameter value of around 50 mu m for all observed powders. Iron-bearing materials like a-Fe2O3 and gamma-Fe2O3 are obtained. Differential thermal analysis curve of obtained samples showed endothermic reaction at 620 oC which could be ascribed to phase transition from cubic form gamma- - GT alpha- Fe2O3. Thermal transformations of iron (III) oxide, obtained from clay as a natural source, is suitable to explore in the framework of materials chemistry, and opens the possibility to synthesize materials based on Fe2O3 with specific magnetic behavior.", journal = "Science of Sintering", title = "Iron (III) Oxide Fabrication From Natural Clay With Reference to Phase Transformation gamma- - GT alpha- Fe2O3", volume = "49", number = "2", pages = "197-205", doi = "10.2298/SOS1702197S" }
Šaponjić, A., Šaponjić, Đ., Nikolić, V. N., Milošević, M., Marinović-Cincović, M., Gyoshev, S., Vuković, M.,& Kokunešoski, M.. (2017). Iron (III) Oxide Fabrication From Natural Clay With Reference to Phase Transformation gamma- - GT alpha- Fe2O3. in Science of Sintering, 49(2), 197-205. https://doi.org/10.2298/SOS1702197S
Šaponjić A, Šaponjić Đ, Nikolić VN, Milošević M, Marinović-Cincović M, Gyoshev S, Vuković M, Kokunešoski M. Iron (III) Oxide Fabrication From Natural Clay With Reference to Phase Transformation gamma- - GT alpha- Fe2O3. in Science of Sintering. 2017;49(2):197-205. doi:10.2298/SOS1702197S .
Šaponjić, Aleksandra, Šaponjić, Đorđe, Nikolić, Violeta N., Milošević, Maja, Marinović-Cincović, Milena, Gyoshev, Stanislav, Vuković, Marina, Kokunešoski, Maja, "Iron (III) Oxide Fabrication From Natural Clay With Reference to Phase Transformation gamma- - GT alpha- Fe2O3" in Science of Sintering, 49, no. 2 (2017):197-205, https://doi.org/10.2298/SOS1702197S . .