Re-formation of metastable epsilon-Fe2O3 in post-annealing of Fe2O3/SiO2 nanostructure: Synthesis, computational particle shape analysis in micrographs and magnetic properties
Samo za registrovane korisnike
2017
Autori
Nikolić, Violeta N.Spasojević, Vojislav
Panjan, Matjaž
Kopanja, Lazar
Mraković, Ana Đ.
Tadić, Marin
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Several Fe2O3/SiO2 nanostructures were synthesized by the combination of the microemulsion and a sol-gel methods. Based on X-ray powder diffraction (XRD) and magnetic measurements (giant coercivity similar to 2.13 T) we identified epsilon-Fe2O3 (hard magnet) as the dominant crystalline phase. TEM analysis showed a wide size distribution of iron oxide nanoparticles (from 4 to 50 nm) with various morphologies (spherical, ellipsoidal and rod-like). We quantitatively described (computational analysis, MATLAB code) morphological properties of nanoparticles using the ellipticity of the shapes. The as-synthesized hard magnetic material was subjected to a post-annealing treatment at different temperatures (200, 500, 750, 1000 and 1100 degrees C) in order to investigate stability, formation and transformation of the epsilon-Fe2O3 polymorph. We found decreasing coercivity in the thermally treated samples up to the temperature of 750 degrees C (H-c=1245 Oe), followed by an observation of a surpri...sing jump in coercivity H-c similar to 1.5 T after post-annealing at 1000 degrees C. We conclude that the re-formation of the epsilon-Fe2O3 structure during post-annealing at 1000 degrees C is the origin of the observed phenomena. The phase transformation epsilon-Fe2O3 - GT alpha-Fe2O3 and crystallization of amorphous silica in quartz and cristobalite were observed in the sample treated at 1100 degrees C.
Ključne reči:
Sol-gel synthesis / epsilon-Fe2O3 / Magnetic properties / Phase transformation / Maghemite (gamma-Fe2O3) / Hematite (alpha-Fe2O3)Izvor:
Ceramics International, 2017, 43, 10, 7497-7507Finansiranje / projekti:
- Magnetni i radionuklidima obeleženi nanostrukturni materijali za primene u medicini (RS-45015)
- Serbian-Slovenian bilateral project [BI-RS/16-17-030]
DOI: 10.1016/j.ceramint.2017.03.030
ISSN: 0272-8842; 1873-3956
WoS: 000400880000017
Scopus: 2-s2.0-85014838558
Kolekcije
Institucija/grupa
VinčaTY - JOUR AU - Nikolić, Violeta N. AU - Spasojević, Vojislav AU - Panjan, Matjaž AU - Kopanja, Lazar AU - Mraković, Ana Đ. AU - Tadić, Marin PY - 2017 UR - https://vinar.vin.bg.ac.rs/handle/123456789/1559 AB - Several Fe2O3/SiO2 nanostructures were synthesized by the combination of the microemulsion and a sol-gel methods. Based on X-ray powder diffraction (XRD) and magnetic measurements (giant coercivity similar to 2.13 T) we identified epsilon-Fe2O3 (hard magnet) as the dominant crystalline phase. TEM analysis showed a wide size distribution of iron oxide nanoparticles (from 4 to 50 nm) with various morphologies (spherical, ellipsoidal and rod-like). We quantitatively described (computational analysis, MATLAB code) morphological properties of nanoparticles using the ellipticity of the shapes. The as-synthesized hard magnetic material was subjected to a post-annealing treatment at different temperatures (200, 500, 750, 1000 and 1100 degrees C) in order to investigate stability, formation and transformation of the epsilon-Fe2O3 polymorph. We found decreasing coercivity in the thermally treated samples up to the temperature of 750 degrees C (H-c=1245 Oe), followed by an observation of a surprising jump in coercivity H-c similar to 1.5 T after post-annealing at 1000 degrees C. We conclude that the re-formation of the epsilon-Fe2O3 structure during post-annealing at 1000 degrees C is the origin of the observed phenomena. The phase transformation epsilon-Fe2O3 - GT alpha-Fe2O3 and crystallization of amorphous silica in quartz and cristobalite were observed in the sample treated at 1100 degrees C. T2 - Ceramics International T1 - Re-formation of metastable epsilon-Fe2O3 in post-annealing of Fe2O3/SiO2 nanostructure: Synthesis, computational particle shape analysis in micrographs and magnetic properties VL - 43 IS - 10 SP - 7497 EP - 7507 DO - 10.1016/j.ceramint.2017.03.030 ER -
@article{ author = "Nikolić, Violeta N. and Spasojević, Vojislav and Panjan, Matjaž and Kopanja, Lazar and Mraković, Ana Đ. and Tadić, Marin", year = "2017", abstract = "Several Fe2O3/SiO2 nanostructures were synthesized by the combination of the microemulsion and a sol-gel methods. Based on X-ray powder diffraction (XRD) and magnetic measurements (giant coercivity similar to 2.13 T) we identified epsilon-Fe2O3 (hard magnet) as the dominant crystalline phase. TEM analysis showed a wide size distribution of iron oxide nanoparticles (from 4 to 50 nm) with various morphologies (spherical, ellipsoidal and rod-like). We quantitatively described (computational analysis, MATLAB code) morphological properties of nanoparticles using the ellipticity of the shapes. The as-synthesized hard magnetic material was subjected to a post-annealing treatment at different temperatures (200, 500, 750, 1000 and 1100 degrees C) in order to investigate stability, formation and transformation of the epsilon-Fe2O3 polymorph. We found decreasing coercivity in the thermally treated samples up to the temperature of 750 degrees C (H-c=1245 Oe), followed by an observation of a surprising jump in coercivity H-c similar to 1.5 T after post-annealing at 1000 degrees C. We conclude that the re-formation of the epsilon-Fe2O3 structure during post-annealing at 1000 degrees C is the origin of the observed phenomena. The phase transformation epsilon-Fe2O3 - GT alpha-Fe2O3 and crystallization of amorphous silica in quartz and cristobalite were observed in the sample treated at 1100 degrees C.", journal = "Ceramics International", title = "Re-formation of metastable epsilon-Fe2O3 in post-annealing of Fe2O3/SiO2 nanostructure: Synthesis, computational particle shape analysis in micrographs and magnetic properties", volume = "43", number = "10", pages = "7497-7507", doi = "10.1016/j.ceramint.2017.03.030" }
Nikolić, V. N., Spasojević, V., Panjan, M., Kopanja, L., Mraković, A. Đ.,& Tadić, M.. (2017). Re-formation of metastable epsilon-Fe2O3 in post-annealing of Fe2O3/SiO2 nanostructure: Synthesis, computational particle shape analysis in micrographs and magnetic properties. in Ceramics International, 43(10), 7497-7507. https://doi.org/10.1016/j.ceramint.2017.03.030
Nikolić VN, Spasojević V, Panjan M, Kopanja L, Mraković AĐ, Tadić M. Re-formation of metastable epsilon-Fe2O3 in post-annealing of Fe2O3/SiO2 nanostructure: Synthesis, computational particle shape analysis in micrographs and magnetic properties. in Ceramics International. 2017;43(10):7497-7507. doi:10.1016/j.ceramint.2017.03.030 .
Nikolić, Violeta N., Spasojević, Vojislav, Panjan, Matjaž, Kopanja, Lazar, Mraković, Ana Đ., Tadić, Marin, "Re-formation of metastable epsilon-Fe2O3 in post-annealing of Fe2O3/SiO2 nanostructure: Synthesis, computational particle shape analysis in micrographs and magnetic properties" in Ceramics International, 43, no. 10 (2017):7497-7507, https://doi.org/10.1016/j.ceramint.2017.03.030 . .