Complex insight into the charge storage behavior of active carbons obtained by carbonization of the plane tree seed
Samo za registrovane korisnike
2016
Autori
Dodevski, VladimirStojmenović, Marija
Vujković, Milica
Krstić, Jugoslav B.
Krstić, Sanja S.
Bajuk-Bogdanović, Danica V.
Kuzmanović, Bojana
Kaluđerović, Branka V.
Mentus, Slavko V.
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Activated carbon was prepared using plane tree seed as a cheap and renewable raw material. The samples were prepared by carbonization under N-2 atmosphere up to 850 degrees C, and activation in CO2 atmosphere at different both temperatures (750 and 850 degrees C) and times of activation (0.3,1 and 2 h). The influence of activation parameters on physicochemical properties was studied by XRPD, Raman spectroscopy, FTIR, N-2 physisorption, SEM and electrochemical methods. The pore structure was correlated to the specific capacitance and the amount of hydrogen stored, in alkaline, neutral and acidic electrolyte solution. The relationship of asymmetrical shape of CV curves with the porosity of samples has served to better understand some unclear issues related to the complex mechanism of charge storage. The sample activated at 850 degrees C for 2 h displayed the best behavior. At a high scan rate of 300 mV s(-1), its capacitance, amounted to similar to 26.8 mu F cm(-2) 19.69 mu F cm(-2) and ...25.8 mu Fcm(-2) in KOH, Na2SO4, and H2SO4 solutions, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Ključne reči:
Activated carbon / Pseudocapacitor / Aqueous neutral electrolyte / Hydrogen storageIzvor:
Electrochimica Acta, 2016, 222, 156-171Finansiranje / projekti:
- Sinteza, procesiranje i karakterizacija nanostrukturnih materijala za primenu u oblasti energije, mehaničkog inženjerstva, zaštite životne stredine i biomedicine (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Funkcionalni, funkcionalizovani i usavršeni nano materijali (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45005)
- Litijum-jon baterije i gorivne ćelije-istraživanje i razvoj (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45014)
- NATO through the Science for Peace Project [EAP.SFPP 984925-DURAPEM]
DOI: 10.1016/j.electacta.2016.10.182
ISSN: 0013-4686; 1873-3859
WoS: 000392566200019
Scopus: 2-s2.0-85005932172
Kolekcije
Institucija/grupa
VinčaTY - JOUR AU - Dodevski, Vladimir AU - Stojmenović, Marija AU - Vujković, Milica AU - Krstić, Jugoslav B. AU - Krstić, Sanja S. AU - Bajuk-Bogdanović, Danica V. AU - Kuzmanović, Bojana AU - Kaluđerović, Branka V. AU - Mentus, Slavko V. PY - 2016 UR - https://vinar.vin.bg.ac.rs/handle/123456789/1396 AB - Activated carbon was prepared using plane tree seed as a cheap and renewable raw material. The samples were prepared by carbonization under N-2 atmosphere up to 850 degrees C, and activation in CO2 atmosphere at different both temperatures (750 and 850 degrees C) and times of activation (0.3,1 and 2 h). The influence of activation parameters on physicochemical properties was studied by XRPD, Raman spectroscopy, FTIR, N-2 physisorption, SEM and electrochemical methods. The pore structure was correlated to the specific capacitance and the amount of hydrogen stored, in alkaline, neutral and acidic electrolyte solution. The relationship of asymmetrical shape of CV curves with the porosity of samples has served to better understand some unclear issues related to the complex mechanism of charge storage. The sample activated at 850 degrees C for 2 h displayed the best behavior. At a high scan rate of 300 mV s(-1), its capacitance, amounted to similar to 26.8 mu F cm(-2) 19.69 mu F cm(-2) and 25.8 mu Fcm(-2) in KOH, Na2SO4, and H2SO4 solutions, respectively. (C) 2016 Elsevier Ltd. All rights reserved. T2 - Electrochimica Acta T1 - Complex insight into the charge storage behavior of active carbons obtained by carbonization of the plane tree seed VL - 222 SP - 156 EP - 171 DO - 10.1016/j.electacta.2016.10.182 ER -
@article{ author = "Dodevski, Vladimir and Stojmenović, Marija and Vujković, Milica and Krstić, Jugoslav B. and Krstić, Sanja S. and Bajuk-Bogdanović, Danica V. and Kuzmanović, Bojana and Kaluđerović, Branka V. and Mentus, Slavko V.", year = "2016", abstract = "Activated carbon was prepared using plane tree seed as a cheap and renewable raw material. The samples were prepared by carbonization under N-2 atmosphere up to 850 degrees C, and activation in CO2 atmosphere at different both temperatures (750 and 850 degrees C) and times of activation (0.3,1 and 2 h). The influence of activation parameters on physicochemical properties was studied by XRPD, Raman spectroscopy, FTIR, N-2 physisorption, SEM and electrochemical methods. The pore structure was correlated to the specific capacitance and the amount of hydrogen stored, in alkaline, neutral and acidic electrolyte solution. The relationship of asymmetrical shape of CV curves with the porosity of samples has served to better understand some unclear issues related to the complex mechanism of charge storage. The sample activated at 850 degrees C for 2 h displayed the best behavior. At a high scan rate of 300 mV s(-1), its capacitance, amounted to similar to 26.8 mu F cm(-2) 19.69 mu F cm(-2) and 25.8 mu Fcm(-2) in KOH, Na2SO4, and H2SO4 solutions, respectively. (C) 2016 Elsevier Ltd. All rights reserved.", journal = "Electrochimica Acta", title = "Complex insight into the charge storage behavior of active carbons obtained by carbonization of the plane tree seed", volume = "222", pages = "156-171", doi = "10.1016/j.electacta.2016.10.182" }
Dodevski, V., Stojmenović, M., Vujković, M., Krstić, J. B., Krstić, S. S., Bajuk-Bogdanović, D. V., Kuzmanović, B., Kaluđerović, B. V.,& Mentus, S. V.. (2016). Complex insight into the charge storage behavior of active carbons obtained by carbonization of the plane tree seed. in Electrochimica Acta, 222, 156-171. https://doi.org/10.1016/j.electacta.2016.10.182
Dodevski V, Stojmenović M, Vujković M, Krstić JB, Krstić SS, Bajuk-Bogdanović DV, Kuzmanović B, Kaluđerović BV, Mentus SV. Complex insight into the charge storage behavior of active carbons obtained by carbonization of the plane tree seed. in Electrochimica Acta. 2016;222:156-171. doi:10.1016/j.electacta.2016.10.182 .
Dodevski, Vladimir, Stojmenović, Marija, Vujković, Milica, Krstić, Jugoslav B., Krstić, Sanja S., Bajuk-Bogdanović, Danica V., Kuzmanović, Bojana, Kaluđerović, Branka V., Mentus, Slavko V., "Complex insight into the charge storage behavior of active carbons obtained by carbonization of the plane tree seed" in Electrochimica Acta, 222 (2016):156-171, https://doi.org/10.1016/j.electacta.2016.10.182 . .