Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains
Аутори
Kokunešoski, MajaBaščarević, Zvezdana D.
Rakočević, Zlatko Lj.
Šaponjić, Aleksandra
Šaponjić, Đorđe
Jordanov, Dragana
Babić, Biljana M.
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials were characterized by XRD, nitrogen adsorption desorption measurements, SEM, EDS and AFM analysis. It was found that small modifications of synthesis conditions influenced the morphological features of the synthesized SBA-15 samples. The SEM analysis had shown that the SBA-15 synthesized at lower temperature and longer time of reaction (80 degrees C, 48 h) provided elongated rod-shaped grains about 1 mu m long. The other sample synthesized at higher temperature and shorter time of reaction (100 degrees C, 24 h) had rounded grains and grains of regular spherical shape with diameters ranging from 0.5 to 2 mu m. The EDS analysis confirmed that the particles of both synthesized samples were of the SiO2 content. In addition, the AFM analysis had shown different surface m...orphologies of the materials synthesized under various conditions.
Кључне речи:
Mesoporous material / SBA-15 / Synthesis conditions / nanostructures / spherical grainsИзвор:
Science of Sintering, 2018, 50, 1, 111-121Финансирање / пројекти:
- Синтеза, процесирање и карактеризација наноструктурних материјала за примену у области енергије, механичког инжењерства, заштите животне стредине и биомедицине (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45012)
- Функционални, функционализовани и усавршени нано материјали (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45005)
- Водонична енергија - развој нових материјала: електролитичко добијање водоника, водоничне горивне ћелије, изотопски ефекти (RS-MESTD-Basic Research (BR or ON)-172045)
DOI: 10.2298/SOS1801111K
ISSN: 0350-820X
WoS: 000429909100010
Scopus: 2-s2.0-85053925810
Колекције
Институција/група
VinčaTY - JOUR AU - Kokunešoski, Maja AU - Baščarević, Zvezdana D. AU - Rakočević, Zlatko Lj. AU - Šaponjić, Aleksandra AU - Šaponjić, Đorđe AU - Jordanov, Dragana AU - Babić, Biljana M. PY - 2018 UR - https://vinar.vin.bg.ac.rs/handle/123456789/7650 AB - Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials were characterized by XRD, nitrogen adsorption desorption measurements, SEM, EDS and AFM analysis. It was found that small modifications of synthesis conditions influenced the morphological features of the synthesized SBA-15 samples. The SEM analysis had shown that the SBA-15 synthesized at lower temperature and longer time of reaction (80 degrees C, 48 h) provided elongated rod-shaped grains about 1 mu m long. The other sample synthesized at higher temperature and shorter time of reaction (100 degrees C, 24 h) had rounded grains and grains of regular spherical shape with diameters ranging from 0.5 to 2 mu m. The EDS analysis confirmed that the particles of both synthesized samples were of the SiO2 content. In addition, the AFM analysis had shown different surface morphologies of the materials synthesized under various conditions. T2 - Science of Sintering T1 - Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains VL - 50 IS - 1 SP - 111 EP - 121 DO - 10.2298/SOS1801111K ER -
@article{ author = "Kokunešoski, Maja and Baščarević, Zvezdana D. and Rakočević, Zlatko Lj. and Šaponjić, Aleksandra and Šaponjić, Đorđe and Jordanov, Dragana and Babić, Biljana M.", year = "2018", abstract = "Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials were characterized by XRD, nitrogen adsorption desorption measurements, SEM, EDS and AFM analysis. It was found that small modifications of synthesis conditions influenced the morphological features of the synthesized SBA-15 samples. The SEM analysis had shown that the SBA-15 synthesized at lower temperature and longer time of reaction (80 degrees C, 48 h) provided elongated rod-shaped grains about 1 mu m long. The other sample synthesized at higher temperature and shorter time of reaction (100 degrees C, 24 h) had rounded grains and grains of regular spherical shape with diameters ranging from 0.5 to 2 mu m. The EDS analysis confirmed that the particles of both synthesized samples were of the SiO2 content. In addition, the AFM analysis had shown different surface morphologies of the materials synthesized under various conditions.", journal = "Science of Sintering", title = "Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains", volume = "50", number = "1", pages = "111-121", doi = "10.2298/SOS1801111K" }
Kokunešoski, M., Baščarević, Z. D., Rakočević, Z. Lj., Šaponjić, A., Šaponjić, Đ., Jordanov, D.,& Babić, B. M.. (2018). Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains. in Science of Sintering, 50(1), 111-121. https://doi.org/10.2298/SOS1801111K
Kokunešoski M, Baščarević ZD, Rakočević ZL, Šaponjić A, Šaponjić Đ, Jordanov D, Babić BM. Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains. in Science of Sintering. 2018;50(1):111-121. doi:10.2298/SOS1801111K .
Kokunešoski, Maja, Baščarević, Zvezdana D., Rakočević, Zlatko Lj., Šaponjić, Aleksandra, Šaponjić, Đorđe, Jordanov, Dragana, Babić, Biljana M., "Influence of synthesis conditions on morphological features of the SBA-15 containing only elongated and rounded/spherical grains" in Science of Sintering, 50, no. 1 (2018):111-121, https://doi.org/10.2298/SOS1801111K . .