The Influence of Mechanical Activation on Sintering Process of BaCO3 -SrCO3 -TiO2 System
(2012)
Poster presented at the conference Advanced Ceramics and Application I - Serbian Ceramic Society, Belgrade May 10-11, 2012
Structural, electrical and magnetic properties of mechanically activated manganese and zinc ferrite
(Belgrade : Institute for Multidisciplinary Research of the University of Belgrade, 2017)
Starting hematite (Fe2O3), zinc oxide (ZnO) and manganese carbonate (MnCO3) powders were homogenized in a planetary ball mill in stainless steel bowls with stainless steel balls for 15 min, calcined in air at 1000 C for ...
Primena Ramanove spektroskopije u proučavanju mehaničke aktivacije BaTiO3
(Beograd : Institut tehničkih nauka SANU, 2006)
U ovom radu su ispitivane strukturne promene BaTiO3 tokom mehaničke aktivacije. Kao početni prah, korišćen je BaTiO3 (Aldrich) prah čistoće 99.9%. Mehanička aktivacija ovog praha izvršena je mlevenjem u visokoenergetskom ...
Surface characterisation of mechanochemicaly activated carbon cloth
(Belgrade : Materials Research Society of Serbia, 2013)
Adsorption on activated carbon cloth is an efficient procedure for removing pollutants from wastewaters, because this material possesses large specific area and high adsorption capacity. Inthis study the activated carbon ...
Synthesis of LiFePO4 by mechanical stressing and thermal annealing
(Belgrade : Materials Research Society of Serbia, 2014)
Mechanical activation can be regarded as a multi-step process with changes in the energetic parameters and the amount of accumulated energy of solids in each step. Here we report the influence of mechanochemical processing ...
Dilatometric Analysis of Mechanically Activated SrTiO3 Powder
(Belgrade : Serbian Ceramic Society, 2013)
Strontium-titanate powder was mechanically activated in a planetary ball mill for 0, 5, 10, 30, 60, 90 and 120 minutes. Non-isothermal sintering of non-activated and activated SrTiO3 powder samples in the temperature ...
Reaction kinetics of mechanically activated cordierite based ceramics studied via DTA
(Ljubljana : Central and Eastern European Committee for Thermal Analysis and Calorimetry, 2015)
Cordierite, 2MgO•2Ah03•5Si02 (MAS), is a very attractive high-temperature ceramic material. In order to accelerate the process of sintering, 5.00 mass% Mo03 was added to the starting mixtures. The mechanical activation of ...
Influence of mechanical activation on the MgO-Al2O3-SiO2 system with TeO2
(Belgrade : Materials Research Society of Serbia, 2016)
Cordierite 2MgO+2Al2O3+5SiO2 is frequently used ceramic material, that is commonly used as a carrier of electrical components due to its low dielectric constant (~ 5), and low temperature thermal expansion coefficient ...
Influence of Mechanical Activation on the Constituents of the MgO-Al2O3-SiO2-TiO2 System
(Belgrade : Serbian Ceramic Society, 2012)
Cordierite, 2MgO2Al2O35SiO2, is a very attractive high-temperature ceramic material, due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good ...
Influence of one activated component on the sintering process of three phase system
(Belgrade : Materials Research Society of Serbia, 2013)
According to its low temperature thermal expansion coefficient, low dielectric constant, also good mechanical properties, cordierite, 2MgO×2Al2O3×5SiO2, represents a very attractive hightemperature ceramic material. In ...