Properties of dispersion-hardened copper made by internal oxidation of prealloyed copper powder containing 2.5wt. % Al
Чланак у часопису
МетаподациПриказ свих података о документу
Prealloyed copper powder containing 2.5wt. %Al was processed in a planetary ball mill to evaluate matrix hardening due to formation of Al2O3 particles in situ by internal oxidation. After milling, the powders were heat treated in hydrogen in order to reduce copper oxide formed on particle surfaces during milling. The compacts were made by hot pressing. The examinations show that the compacts possess a good combination of high strength and high electrical conductivities. After 5h of milling the microhardness of the prealloyed compact was 3 to 4 times higher than that of the as-received electrolytic copper compacted under the same conditions, while the conductivity was 68% IACS. Also, it was found that the prealloyed compacts preserved much of the hardness after exposure to high temperature in inert atmospheres.
Кључне речи:copper matrix hardening / dispersion-hardened copper / high energy ball milling / internal oxidation in air
Извор:Materials Science Forum, 2005, 494, 493-497
- Current Research in Advanced Materials and Processes, 6th Conference of the Yugoslav-Materials-Research-Society, Sep 13-17, 2004, Herceg Novi, Montenegro
ISSN: 0255-5476 (print)