dc.description.abstractNanocrystalline up-converting Y2O3:Yb3+, Er3+ phosphor particles were processed in a dispersed system-aerosol, generated ultrasonically at 1.3 MHz from common nitrate precursor solution having fixed ytterbium-to-erbium concentration ratio. The appropriate process parameters: residence time 21 s, carrier gas (air) flow rate 1.6 dm(3)/min, synthesis temperature 900 degrees C, led to the formation of un-agglomerated spherical nanostructured secondary particles, having mean particle size of approx 450 nm, composed of primary nanoscaled (20 nm) subunits. In order to reach targeting phase crystallinity, the as-prepared particles were additionally annealed at 1100 degrees C in air for 12, 24 and 48 h, respectively. Particle structure, morphology and purity were analyzed by X-ray powder diffraction (XRPD), scanning electron microscopy (FESEM/SEM), analytical and high resolution transmission electron microscopy (TEM/HRTEM) in combination with energy dispersive X-ray analysis and Fourier Transform Infrared Spectroscopy (FTIR). All samples crystallized in a cubic bixbyte-structure, space group Ia-3. The crystallite size changed with annealing time from 30 nm in as-prepared sample to 135 nm in sample annealed for 48 h, respectively. Emission spectra were assigned to the following trivalent erbium f-f electronic transitions: H-2(9/2) - GT I-4(15/2) (blue: 407-420 nm), (H-2(11/2), S-4(3/2)) - GT I-4(15/2) (green: 510-590 nm), and F-4(9/2) - GT I-4(15/2) (red: 640-720 nm). The significant improvement of the emission decay times were observed after thermal treatment and this effect is correlated further with the structural and morphological particles characteristics. For the annealing time of 12 h a quite high emission decay times were achieved (blue: 0.14 ms, green: 0.32 ms and red: 0.39 ms).en
dc.relationinfo:eu-repo/grantAgreement/MESTD/Basic Research (BR or ON)/172035/RS//
dc.rightsrestrictedAccessen
dc.sourceJournal of Alloys and Compoundsen
dc.subjectAerosol processingen
dc.subjectNanoparticlesen
dc.subjectY2O3en
dc.subjectUp-conversionen
dc.subjectDecay timeen
dc.titleStructural, morphological and luminescence properties of nanocrystalline up-converting Y1.89Yb0.1Er0.01O3 phosphor particles synthesized through aerosol routeen
dc.typearticleen
dc.rights.licenseARR
dcterms.abstractТан, З.; Манциц, Л.; Драмићанин Мирослав; Милосевиц, О.; Охара, С.; Рабанал, М. Е.; Хасхисхин, Т.; Лојпур Весна;
dc.rights.holder© 2013 Elsevier B.V
dc.citation.volume580
dc.citation.spage584
dc.citation.epage591
dc.identifier.wos000324525800092
dc.identifier.doi10.1016/j.jallcom.2013.07.125
dc.citation.rankM21a
dc.description.otherPeer-reviewed version of the article (Accepted Manuscript or postprint) available at: [https://vinar.vin.bg.ac.rs/handle/123456789/7992]
dc.type.versionpublishedVersion
dc.identifier.scopus2-s2.0-84882315913


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу