dc.description.abstractDue to its characteristics, cordierite, 2MgO center dot 2Al(2)O(3)center dot 5SiO(2), is a high-temperature ceramic material of a great scientific interest. Mechanical activation of the starting mixtures containing 5.00 mass% TiO2 was performed in a high-energy ball mill for 10 minutes. The compaction pressure varied from 0.5 to 6tcm(-2) (49-588 MPa). The sintering process was performed at 1350 degrees C for four hours in the air atmosphere. The phase composition of the activated and sintered samples was analyzed using X-ray diffraction. Scanning electron microscopy was used to analyze the microstructure of both compacted and sintered samples. The authors have investigated the influence of compaction pressure on the sintered samples and their electrical properties.en
dc.rightsopenAccessen
dc.sourceScience of Sinteringen
dc.subjectMechanical activationen
dc.subjectDensityen
dc.subjectXRDen
dc.subjectSEMen
dc.subjectElectrical propertiesen
dc.subjectCordieriteen
dc.titleThe Influence of Compaction Pressure on the Density and Electrical Properties of Cordierite-based Ceramicsen
dc.typearticleen
dcterms.abstractДордевиц, Н.; Филиповиц, С.; Пелес, A.; Обрадовиц, Н.; Павловиц, В. Б.; Митрић Миодраг;
dc.citation.volume47
dc.citation.issue1
dc.citation.spage15
dc.citation.epage22
dc.identifier.wos000355226700003
dc.identifier.doi10.2298/SOS1501015O
dc.citation.rankM23
dc.identifier.scopus2-s2.0-84928801823
dc.identifier.fulltexthttp://vinar.vin.bg.ac.rs//bitstream/id/13482/561.pdf


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record