Surface modification of submicronic TiO2 particles prepared by ultrasonic spray pyrolysis for visible light absorption
АуториDugandzic, Ivan M.
Jovanović, Dragana J.
Mancic, Lidija T.
Ahrenkiel, Scott Phillip
Milosevic, Olivera B.
Чланак у часопису
МетаподациПриказ свих података о документу
Spherical, submicronic TiO2 assemblage with high specific surface area and controllable phase composition was prepared in the process of ultrasonic spray drying/pyrolysis in a wide temperature range (150-800 degrees C) by using as a precursor aqueous colloidal solution consisting of TiO2 nanoparticles (4.5 nm). Submicronic, soft and grained spherical TiO2 particles (d = 370-500 nm) comprising clustered nanocrystals ( LT 10 nm) were obtained at low processing temperature, while particle densification, intensive growth of the clustered primary units and anatase-to-rutile transformation (similar to 30 wt%) were observed at the higher temperatures. Detailed structural and morphological characterisation were performed by X-ray powder diffraction, scanning and field emission electron microscopy, transmission electron microscopy, and laser particle size analysis. Moreover, the surface modification of TiO2 particles through the formation of charge-transfer (CT) complex was achieved with differ...ent ligands: ascorbic acid, dopamine, catechol, 2,3-dihydroxynaphthalene, and anthrarobin. Optical properties of the surface-modified TiO2 particles were studied by using diffuse reflection spectroscopy. The binding structure between the surface titanium atoms and different ligands was determined by using Fourier transform infrared spectroscopy. The formation of CT complexes induced significant red shift of optical absorption in comparison to unmodified TiO2 particles.
Кључне речи:TiO2 nanoparticles / Spray drying/pyrolysis / Surface modification / Charge-transfer complex / Optical properties
Извор:Journal of Nanoparticle Research, 2012, 14, 10
- Материјали редуковане димензионалности за ефикасну апсорпцију светлости и конверзију енергије (RS-45020)
ISSN: 1388-0764 (print)