Isothermal sintering of barium-zinc-titanate ceramics
Pavlović, Vladimir B.
Ristic, M. M.
Чланак у часопису
МетаподациПриказ свих података о документу
Mixtures of BaCO(3)-ZnO-TiO(2) were mechanically activated using high-energy planetary ball mill during 20, 40 and 80 min. As the time of mechanical activation increased, the decrease in particle size was observed. The effect of milling on microstructure was investigated by scanning electron microscopy, as well. Sintering process was performed in air at 1100 and 1200 C for 2 h. Various phases are present within mixtures sintered at 1100 and 1200 degrees C, and almost pure BaZn(2)Ti(4)O(11) phase was obtained after 80 min of milling and sintering at 1200 degrees C for 2 h. (C) 2010 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Кључне речи:Milling / Sintering / X-ray methods / Traditional ceramics
Извор:Ceramics International, 2011, 37, 1, 21-27