Advantages of Combined Sintering Compared to Conventional Sintering of Mechanically Activated Magnesium Titanate
2014
Аутори
Filipović, SuzanaObradović, Nina
Pavlović, Vladimir B.
Kosanović, Darko
Mitrić, Miodrag
Mitrovic, N.
Pouchly, V.
Kachlik, M.
Maca, Karel
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
In this article, the advantages of combined sintering in comparison with the conventional one, of mechanically activated magnesium titanate ceramic were investigated. The stoichiometric mixtures of MgO and TiO2 were mechano-chemically activated for 0, 10, 40, 80 and 160 minutes by ball milling and then isostatically pressed (CIP) to form green bodies. Conventional sintering was realized by heating up to 1400 degrees C and hold for 30 minutes in air atmosphere. Resulting ceramic samples with closed porosity were post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1280 degrees C/3h in argon atmosphere with a pressure of 200 MPa. The best results were observed in the case of samples post-sintered by HIP, when single-phase MgTiO3 samples with relative density of 96% were prepared.
Кључне речи:
Sintering / Ceramics / Magnesium titanateИзвор:
Science of Sintering, 2014, 46, 3, 283-290Финансирање / пројекти:
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-MESTD-Basic Research (BR or ON)-172057)
- Serbian Academy of Science and Arts [F/198], European Regional Development Fund through a project CEITEC [CZ.1.05/1.1.00/02.0068]
DOI: 10.2298/SOS1403283F
ISSN: 0350-820X
WoS: 000348599200002
Scopus: 2-s2.0-84920937736
Колекције
Институција/група
VinčaTY - JOUR AU - Filipović, Suzana AU - Obradović, Nina AU - Pavlović, Vladimir B. AU - Kosanović, Darko AU - Mitrić, Miodrag AU - Mitrovic, N. AU - Pouchly, V. AU - Kachlik, M. AU - Maca, Karel PY - 2014 UR - https://vinar.vin.bg.ac.rs/handle/123456789/373 AB - In this article, the advantages of combined sintering in comparison with the conventional one, of mechanically activated magnesium titanate ceramic were investigated. The stoichiometric mixtures of MgO and TiO2 were mechano-chemically activated for 0, 10, 40, 80 and 160 minutes by ball milling and then isostatically pressed (CIP) to form green bodies. Conventional sintering was realized by heating up to 1400 degrees C and hold for 30 minutes in air atmosphere. Resulting ceramic samples with closed porosity were post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1280 degrees C/3h in argon atmosphere with a pressure of 200 MPa. The best results were observed in the case of samples post-sintered by HIP, when single-phase MgTiO3 samples with relative density of 96% were prepared. T2 - Science of Sintering T1 - Advantages of Combined Sintering Compared to Conventional Sintering of Mechanically Activated Magnesium Titanate VL - 46 IS - 3 SP - 283 EP - 290 DO - 10.2298/SOS1403283F ER -
@article{ author = "Filipović, Suzana and Obradović, Nina and Pavlović, Vladimir B. and Kosanović, Darko and Mitrić, Miodrag and Mitrovic, N. and Pouchly, V. and Kachlik, M. and Maca, Karel", year = "2014", abstract = "In this article, the advantages of combined sintering in comparison with the conventional one, of mechanically activated magnesium titanate ceramic were investigated. The stoichiometric mixtures of MgO and TiO2 were mechano-chemically activated for 0, 10, 40, 80 and 160 minutes by ball milling and then isostatically pressed (CIP) to form green bodies. Conventional sintering was realized by heating up to 1400 degrees C and hold for 30 minutes in air atmosphere. Resulting ceramic samples with closed porosity were post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1280 degrees C/3h in argon atmosphere with a pressure of 200 MPa. The best results were observed in the case of samples post-sintered by HIP, when single-phase MgTiO3 samples with relative density of 96% were prepared.", journal = "Science of Sintering", title = "Advantages of Combined Sintering Compared to Conventional Sintering of Mechanically Activated Magnesium Titanate", volume = "46", number = "3", pages = "283-290", doi = "10.2298/SOS1403283F" }
Filipović, S., Obradović, N., Pavlović, V. B., Kosanović, D., Mitrić, M., Mitrovic, N., Pouchly, V., Kachlik, M.,& Maca, K.. (2014). Advantages of Combined Sintering Compared to Conventional Sintering of Mechanically Activated Magnesium Titanate. in Science of Sintering, 46(3), 283-290. https://doi.org/10.2298/SOS1403283F
Filipović S, Obradović N, Pavlović VB, Kosanović D, Mitrić M, Mitrovic N, Pouchly V, Kachlik M, Maca K. Advantages of Combined Sintering Compared to Conventional Sintering of Mechanically Activated Magnesium Titanate. in Science of Sintering. 2014;46(3):283-290. doi:10.2298/SOS1403283F .
Filipović, Suzana, Obradović, Nina, Pavlović, Vladimir B., Kosanović, Darko, Mitrić, Miodrag, Mitrovic, N., Pouchly, V., Kachlik, M., Maca, Karel, "Advantages of Combined Sintering Compared to Conventional Sintering of Mechanically Activated Magnesium Titanate" in Science of Sintering, 46, no. 3 (2014):283-290, https://doi.org/10.2298/SOS1403283F . .