dc.description.abstractPorous silica ceramics were obtained at low forming pressure (40-80 MPa) and low sintering temperature (850-1300 degrees C) for 4 h in air. Boric acid was used as a low-cost additive, in the amount of 2 wt%. Relatively high porosities of nearly 40% and 65% are obtained for the samples of clay and diatomite pressed at 40 MPa, and sintered at 1000 degrees C, respectively. The samples sintered at 1150 degrees C and 1300 degrees C have the average pore size diameters in the range of macroporous for clay 0.2-10 m and for diatomite 0.2-5 m. X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, and mercury porosimetry measurements were employed to characterize of the obtained samples. Measurements of densities and open porosities by immersion technique were used, according to the Archimedes principle. The relations between mechanical characteristics of the samples formed by using different pressures and sintered at different temperature, were discussed.en
dc.relationinfo:eu-repo/grantAgreement/MESTD/Integrated and Interdisciplinary Research (IIR or III)/45012/RS//
dc.rightsrestrictedAccessen
dc.sourceCeramics Internationalen
dc.subjectSinteringen
dc.subjectPorosityen
dc.subjectClaysen
dc.subjectDiatomiteen
dc.subjectBoric aciden
dc.titleEffect of boric acid on the porosity of clay and diatomite monolithsen
dc.typearticleen
dc.rights.licenseARR
dcterms.abstractСтанковиц, Мирослав; Кокунешоски Маја; Мајсторовиц, Јелена; Егеља Aдела; Шапоњић, Aлександра; Илић Светлана; Матовић Бранко;
dc.citation.volume42
dc.citation.issue5
dc.citation.spage6383
dc.citation.epage6390
dc.identifier.wos000370884500094
dc.identifier.doi10.1016/j.ceramint.2016.01.034
dc.citation.rankM21
dc.type.versionpublishedVersion
dc.identifier.scopus2-s2.0-84955316901


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу