Crystallographic orientations of Ni3Al-based aluminide
Чланак у часопису
МетаподациПриказ свих података о документу
Inverse pole figures have been plotted to determine preferred crystallographic orientations in a powder-compacted Ni3Al aluminide prealloyed with Fe, Ti and B. The main textural components, although weak, were noticeably altered by cold deformation, recrystallization and high-temperature deformation. Cold uniaxial compression generated a pronounced (110) orientation and the less common (112) orientation. The existence of the latter orientation was ascribed to the cubic -- GT tetragonal structural transformation (Ll(2) -- GT DO22) The beginning of recrystallization was characterized by a string of (113)+(112)+(111) orientations. However, after prolonged periods of annealing, the (113) orientation diminished, whereas the (111) and (112) orientations became stronger, perhaps due to preferred orientational growth. Deformation at high-temperature gave rise to strong (111) and (100)+(112) orientations. It was found that disordering and dynamic recrystallization simultaneously control high-te...mperature deformation. (C) 2000 Elsevier Science Inc. All rights reserved.
Извор:Materials Characterization, 2000, 45, 3, 227-231
ISSN: 1044-5803 (print)