Structural and morphological characterization of iron-doped sol-gel derived mullite powders
Само за регистроване кориснике
2020
Аутори
Ilić, Svetlana M.Babić, Biljana M.
Bjelajac, Anđelika
Stoimenov, Nikolay
Kljajević, Ljiljana M.
Pošarac-Marković, Milica B.
Matović, Branko
Чланак у часопису (Објављена верзија)
,
© 2020 Elsevier Ltd and Techna Group S.r.l.
Метаподаци
Приказ свих података о документуАпстракт
The structural and morphological properties of iron-doped mullite powders are the subject of the present study. The powders of undoped and iron-doped mullite in the composition range of 3–15 wt% Fe2O3 were synthesized by a combination of sol-gel and combustion methods. The excess of water and urea were introduced in reaction solutions to enhance the copolymerization of aluminum and silicon species. The results of structural characterization revealed that the synthesized mullite powders were amorphous of a hybrid type. The specific surface area of the undoped mullite powder was 262 m2 g-1 with a maximum pore radius (dp) of 2 nm classifying it into mesoporous materials. The addition of iron has reduced the specific surface area, while the pore size value remained the same except for the sample with 3 wt% Fe2O3 (SBET = 278 m2 g-1; dp = 3 nm). The presence of iron caused lowering the temperature of liquid phase formation, while present urea combusted providing the increase of the temperatu...re locally that caused the sintering and formation of agglomerates of smaller particles. However, the results of the particle size analysis are not straightforward. The values of mean volume diameter (D[3,4]) indicated that the particle size increased to 6 wt% Fe2O3 (123.6 μm), and then decreased and for the sample with 12 wt% Fe2O3, it was equal to 96.6 μm. Thus, the added iron contributed to the more uniform particle size distribution. The SEM analysis has also shown the coarse powder particles consisted of the coalesced smaller particles. © 2020 Elsevier Ltd and Techna Group S.r.l.
Кључне речи:
Powders / Chemical preparation / Sol-gel processes / Mullite / PorosityИзвор:
Ceramics International, 2020, 46, 9, 13107-13113Финансирање / пројекти:
DOI: 10.1016/j.ceramint.2020.02.083
ISSN: 0272-8842
WoS: 000551128800026
Scopus: 2-s2.0-85079431205
Колекције
Институција/група
VinčaTY - JOUR AU - Ilić, Svetlana M. AU - Babić, Biljana M. AU - Bjelajac, Anđelika AU - Stoimenov, Nikolay AU - Kljajević, Ljiljana M. AU - Pošarac-Marković, Milica B. AU - Matović, Branko PY - 2020 UR - https://vinar.vin.bg.ac.rs/handle/123456789/8823 AB - The structural and morphological properties of iron-doped mullite powders are the subject of the present study. The powders of undoped and iron-doped mullite in the composition range of 3–15 wt% Fe2O3 were synthesized by a combination of sol-gel and combustion methods. The excess of water and urea were introduced in reaction solutions to enhance the copolymerization of aluminum and silicon species. The results of structural characterization revealed that the synthesized mullite powders were amorphous of a hybrid type. The specific surface area of the undoped mullite powder was 262 m2 g-1 with a maximum pore radius (dp) of 2 nm classifying it into mesoporous materials. The addition of iron has reduced the specific surface area, while the pore size value remained the same except for the sample with 3 wt% Fe2O3 (SBET = 278 m2 g-1; dp = 3 nm). The presence of iron caused lowering the temperature of liquid phase formation, while present urea combusted providing the increase of the temperature locally that caused the sintering and formation of agglomerates of smaller particles. However, the results of the particle size analysis are not straightforward. The values of mean volume diameter (D[3,4]) indicated that the particle size increased to 6 wt% Fe2O3 (123.6 μm), and then decreased and for the sample with 12 wt% Fe2O3, it was equal to 96.6 μm. Thus, the added iron contributed to the more uniform particle size distribution. The SEM analysis has also shown the coarse powder particles consisted of the coalesced smaller particles. © 2020 Elsevier Ltd and Techna Group S.r.l. T2 - Ceramics International T1 - Structural and morphological characterization of iron-doped sol-gel derived mullite powders VL - 46 IS - 9 SP - 13107 EP - 13113 DO - 10.1016/j.ceramint.2020.02.083 ER -
@article{ author = "Ilić, Svetlana M. and Babić, Biljana M. and Bjelajac, Anđelika and Stoimenov, Nikolay and Kljajević, Ljiljana M. and Pošarac-Marković, Milica B. and Matović, Branko", year = "2020", abstract = "The structural and morphological properties of iron-doped mullite powders are the subject of the present study. The powders of undoped and iron-doped mullite in the composition range of 3–15 wt% Fe2O3 were synthesized by a combination of sol-gel and combustion methods. The excess of water and urea were introduced in reaction solutions to enhance the copolymerization of aluminum and silicon species. The results of structural characterization revealed that the synthesized mullite powders were amorphous of a hybrid type. The specific surface area of the undoped mullite powder was 262 m2 g-1 with a maximum pore radius (dp) of 2 nm classifying it into mesoporous materials. The addition of iron has reduced the specific surface area, while the pore size value remained the same except for the sample with 3 wt% Fe2O3 (SBET = 278 m2 g-1; dp = 3 nm). The presence of iron caused lowering the temperature of liquid phase formation, while present urea combusted providing the increase of the temperature locally that caused the sintering and formation of agglomerates of smaller particles. However, the results of the particle size analysis are not straightforward. The values of mean volume diameter (D[3,4]) indicated that the particle size increased to 6 wt% Fe2O3 (123.6 μm), and then decreased and for the sample with 12 wt% Fe2O3, it was equal to 96.6 μm. Thus, the added iron contributed to the more uniform particle size distribution. The SEM analysis has also shown the coarse powder particles consisted of the coalesced smaller particles. © 2020 Elsevier Ltd and Techna Group S.r.l.", journal = "Ceramics International", title = "Structural and morphological characterization of iron-doped sol-gel derived mullite powders", volume = "46", number = "9", pages = "13107-13113", doi = "10.1016/j.ceramint.2020.02.083" }
Ilić, S. M., Babić, B. M., Bjelajac, A., Stoimenov, N., Kljajević, L. M., Pošarac-Marković, M. B.,& Matović, B.. (2020). Structural and morphological characterization of iron-doped sol-gel derived mullite powders. in Ceramics International, 46(9), 13107-13113. https://doi.org/10.1016/j.ceramint.2020.02.083
Ilić SM, Babić BM, Bjelajac A, Stoimenov N, Kljajević LM, Pošarac-Marković MB, Matović B. Structural and morphological characterization of iron-doped sol-gel derived mullite powders. in Ceramics International. 2020;46(9):13107-13113. doi:10.1016/j.ceramint.2020.02.083 .
Ilić, Svetlana M., Babić, Biljana M., Bjelajac, Anđelika, Stoimenov, Nikolay, Kljajević, Ljiljana M., Pošarac-Marković, Milica B., Matović, Branko, "Structural and morphological characterization of iron-doped sol-gel derived mullite powders" in Ceramics International, 46, no. 9 (2020):13107-13113, https://doi.org/10.1016/j.ceramint.2020.02.083 . .