Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions
Само за регистроване кориснике
2016
Аутори
Božanić, Dušan K.Draganić, Ilija
Bibić, Nataša M.
Luyt, Adriaan S.
Konstantinović, Zorica
Đoković, Vladimir
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Ethylene-co-vinyl acetate/iron nanocomposite films were fabricated by implantation with multiple charged ions at different fluencies. The films obtained with ion fluency of 1 x 10(17) cm(-2) were used for specific studies. It was found that spherical similar to 1.5 nm diameter nanoparticles were formed upon implantation. They were clustered into a single 80 nm wide strip about 40 nm beneath the film surface. The magnetic measurements of the film showed that the particles exhibit superparamagnetic behavior with a blocking temperature below 5K. A second type of the samples was also prepared with ion fluency of 1 x 10(17) cm(-2), but prior to implantation, the iron was evaporated onto the co-polymer surface. A nanocomposite film of different morphology was obtained upon the implantation and the particles were much smaller (-0.8 nm). The magnetic behavior of both the films was that of isolated nanoparticles, despite the high ion fluency of 1 x 10(17) cm(-2). (C) 2016 Elsevier B.V. All righ...ts reserved.
Кључне речи:
Ion implantation / Nanocomposite / Iron Multiple charged ions / Magnetic properties / Ion beam mixingИзвор:
Applied Surface Science, 2016, 378, 362-367Издавач:
- Elsevier
Финансирање / пројекти:
- Материјали редуковане димензионалности за ефикасну апсорпцију светлости и конверзију енергије (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45020)
- Утицај величине, облика и структуре наночестица на њихова својства и својства нанокомпозита (RS-MESTD-Basic Research (BR or ON)-172056)
- Наноструктурни мултифункционални материјали и нанокомпозити (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45018)
DOI: 10.1016/j.apsusc.2016.04.020
ISSN: 0169-4332
WoS: 000376819200046
Scopus: 2-s2.0-84963718645
Колекције
Институција/група
VinčaTY - JOUR AU - Božanić, Dušan K. AU - Draganić, Ilija AU - Bibić, Nataša M. AU - Luyt, Adriaan S. AU - Konstantinović, Zorica AU - Đoković, Vladimir PY - 2016 UR - https://vinar.vin.bg.ac.rs/handle/123456789/1097 AB - Ethylene-co-vinyl acetate/iron nanocomposite films were fabricated by implantation with multiple charged ions at different fluencies. The films obtained with ion fluency of 1 x 10(17) cm(-2) were used for specific studies. It was found that spherical similar to 1.5 nm diameter nanoparticles were formed upon implantation. They were clustered into a single 80 nm wide strip about 40 nm beneath the film surface. The magnetic measurements of the film showed that the particles exhibit superparamagnetic behavior with a blocking temperature below 5K. A second type of the samples was also prepared with ion fluency of 1 x 10(17) cm(-2), but prior to implantation, the iron was evaporated onto the co-polymer surface. A nanocomposite film of different morphology was obtained upon the implantation and the particles were much smaller (-0.8 nm). The magnetic behavior of both the films was that of isolated nanoparticles, despite the high ion fluency of 1 x 10(17) cm(-2). (C) 2016 Elsevier B.V. All rights reserved. PB - Elsevier T2 - Applied Surface Science T1 - Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions VL - 378 SP - 362 EP - 367 DO - 10.1016/j.apsusc.2016.04.020 ER -
@article{ author = "Božanić, Dušan K. and Draganić, Ilija and Bibić, Nataša M. and Luyt, Adriaan S. and Konstantinović, Zorica and Đoković, Vladimir", year = "2016", abstract = "Ethylene-co-vinyl acetate/iron nanocomposite films were fabricated by implantation with multiple charged ions at different fluencies. The films obtained with ion fluency of 1 x 10(17) cm(-2) were used for specific studies. It was found that spherical similar to 1.5 nm diameter nanoparticles were formed upon implantation. They were clustered into a single 80 nm wide strip about 40 nm beneath the film surface. The magnetic measurements of the film showed that the particles exhibit superparamagnetic behavior with a blocking temperature below 5K. A second type of the samples was also prepared with ion fluency of 1 x 10(17) cm(-2), but prior to implantation, the iron was evaporated onto the co-polymer surface. A nanocomposite film of different morphology was obtained upon the implantation and the particles were much smaller (-0.8 nm). The magnetic behavior of both the films was that of isolated nanoparticles, despite the high ion fluency of 1 x 10(17) cm(-2). (C) 2016 Elsevier B.V. All rights reserved.", publisher = "Elsevier", journal = "Applied Surface Science", title = "Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions", volume = "378", pages = "362-367", doi = "10.1016/j.apsusc.2016.04.020" }
Božanić, D. K., Draganić, I., Bibić, N. M., Luyt, A. S., Konstantinović, Z.,& Đoković, V.. (2016). Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions. in Applied Surface Science Elsevier., 378, 362-367. https://doi.org/10.1016/j.apsusc.2016.04.020
Božanić DK, Draganić I, Bibić NM, Luyt AS, Konstantinović Z, Đoković V. Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions. in Applied Surface Science. 2016;378:362-367. doi:10.1016/j.apsusc.2016.04.020 .
Božanić, Dušan K., Draganić, Ilija, Bibić, Nataša M., Luyt, Adriaan S., Konstantinović, Zorica, Đoković, Vladimir, "Morphology and magnetic properties of the ethylene-co-vinyl acetate/iron nanocomposite films prepared by implantation with Fe6+ ions" in Applied Surface Science, 378 (2016):362-367, https://doi.org/10.1016/j.apsusc.2016.04.020 . .